- 熔体流动速率 [g/10min]: 5.5
- 密度 [g/cm3]: 1.216
- 吸水率 [%]: 0.1
- 缺口冲击强度: 52.9
- 拉伸强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 1.674
- 热变形温度 [℃]: 86.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 | ||
| Density | 1.216 g/cc | 0.04393 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.100 % | 0.100 % | 24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0180 cm/cm | 0.0180 in/in | ASTM D955 | ||
| 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 | ||
| Melt Flow | 5.50 g/10 min @Load 5.00 kg, Temperature 250 °C | 5.50 g/10 min @Load 11.0 lb, Temperature 482 °F | (MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 38.0 | 38.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 29.0 MPa | 4210 psi | 50mm/min; ISO 527-2/1A | ||
| Tensile Stress | 26.0 MPa @Strain 50.0 % | 3770 psi @Strain 50.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50mm/min; ISO 527-2/1A | ||
| 43.4 MPa | 6300 psi | ASTM D638 | |||
| Elongation at Break | 174 % | 174 % | 50mm/min; ISO 527-2/1A | ||
| 247 % | 247 % | 50mm/min; ISO 527-2/1A | |||
| 150 % @Temperature 22.8 °C | 150 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 4.40 % | 4.40 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.763 GPa | 255.7 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 47.0 MPa | 6820 psi | ISO 178 | ||
| 60.0 MPa | 8700 psi | ASTM D790 | |||
| Flexural Modulus | 1.674 GPa | 242.8 ksi | ISO 178 | ||
| 1.93 GPa @Temperature 22.8 °C | 280 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 52.9 J/cm | 99.0 ft-lb/in | ASTM D256 | ||
| 1.60 J/cm @Temperature -28.9 °C | 3.00 ft-lb/in @Temperature -20.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eA | ||
| 1.90 J/cm² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.00 @Frequency 100 Hz | 4.00 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00700 @Frequency 100 Hz | 0.00700 @Frequency 100 Hz | IEC 60250 | ||
| 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75-1, -2 | ||
| 104 °C | 220 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 | ||
| 51.0 °C | 124 °F | ISO 75-1, -2 | |||
| Vicat Softening Point | 128 °C | 262 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 240 - 265 °C | 464 - 509 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 240 - 265 °C | 464 - 509 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Screw Speed - Moderate | |||||