- 密度 [g/cm3]: 1.34
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 14.0 % | 14.0 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1mm/min; ISO 527-2/1A |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |