- 密度 [g/cm3]: 1.4
- 弯曲模量 [MPa]: 5.16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 94.0 MPa | 13600 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.8 % | 3.8 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 5.47 GPa | 793 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 138 MPa | 20000 psi | ISO 178 |
| Flexural Modulus | 5.16 GPa | 748 ksi | ISO 178 |
| Charpy Impact, Notched | 0.420 J/cm² | 2.00 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 224 °C | 435 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ISO 75-1, -2 |