- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 6.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 82 | 82 | ISO 2039-2 | ||
| Tensile Strength at Break | 88.0 MPa | 12800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.7 % | 2.7 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 6.90 GPa | 1000 ksi | 1mm/min; ISO 527-2/1A | ||
| Izod Impact, Notched (ISO) | 6.90 kJ/m² | 3.28 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.620 J/cm² | 2.95 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 6.00e+16 ohm | 6.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 206 °C | 403 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |||
| Descriptive Properties | |||||
| Melt volume rate (MVR), cm³/10min | 5.6 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||