- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 0.07
- 缺口冲击强度: 8.4
- 弯曲强度 [MPa]: 140.0
- 弯曲模量 [MPa]: 10.6
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ISO 2039-2 |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 225 MPa | 32600 psi | ISO 178 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.40 kJ/m² | 4.00 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.9 @Frequency 100 Hz | 3.9 @Frequency 100 Hz | |
| Dielectric Strength | 19.0 kV/mm @Thickness 3.17 mm | 483 kV/in @Thickness 0.125 in | 50% RH; ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 100 Hz | 0.0060 @Frequency 100 Hz | |
| Comparative Tracking Index | 280 V | 280 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |