- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 3.8
- 拉伸强度 [MPa]: 79.3
- 断裂伸长率 [%]: 110
- 弯曲模量 [MPa]: 3.45
- 热变形温度 [℃]: 206.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 66.9 MPa | 9700 psi | ASTM D638 |
| 78.0 MPa | 11300 psi | 5 mm/min; ISO 527-2/1A | |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min; ISO 527-2/1A |
| 8.5 % | 8.5 % | ASTM D638 | |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| 3.55 GPa | 515 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 3.80 kJ/m² | 1.81 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 19.0 J/cm² @Temperature -30.0 °C | 90.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | IEC 60250 |
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 18.5 kV/mm | 470 kV/in | Short Term; ASTM D149 |
| 23.0 kV/mm | 584 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0013 @Frequency 100 Hz | 0.0013 @Frequency 100 Hz | IEC 60250 |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 60250 | |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 130 µm/m-°C @Temperature 20.0 °C | 72.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,2,3 & ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Mold Temperature | 65.0 - 93.0 °C | 149 - 199 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |