- 熔体流动速率 [g/10min]: 18.08
- 密度 [g/cm3]: 1.13
- 拉伸强度 [MPa]: 40.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Melt Flow | 18.08 g/10 min @Load 2.16 kg, Temperature 250 °C | 18.08 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| 50.85 g/10 min @Load 5.00 kg, Temperature 250 °C | 50.85 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | |
| 158.2 g/10 min @Load 10.0 kg, Temperature 260 °C | 158.2 g/10 min @Load 22.0 lb, Temperature 500 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527-1/2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature 23.0 - 80.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 80.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 135 °C | 275 °F | Method B, 50 N; ISO 306 |
| 180 °C | 356 °F | Method A, 10 N; ISO 306 | |