- 密度 [g/cm3]: 1.67
- 拉伸强度 [MPa]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.002 cm/cm @Thickness 2.00 mm | 0.002 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 84 | 84 | ISO 868 | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527-1/2 | ||
| Elongation at Break | 2.3 % | 2.3 % | ISO 527-1/2 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | ||
| 4.4 @Frequency 1e+6 Hz | 4.4 @Frequency 1e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz | 0.0030 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | 100 drops value; IEC 60112 | ||
| 275 V | 275 V | Test Solution A CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 213 °C | 415 °F | Method B, 50 N; ISO 306 | ||
| 220 °C | 428 °F | Method A, 10 N; ISO 306 | |||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | IEC 60695 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695 | |||
| Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-1/0-3 | ||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 | IEC 60426 | |||