- 缺口冲击强度: 0.8
- 弯曲模量 [MPa]: 9.50
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc @Temperature 23.0 °C | 1.41 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C | 0.0050 - 0.0070 in/in @Temperature 73.4 °F | Plumb; ASTM D955 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Temperature 23.0 °C | 0.0020 - 0.0030 in/in @Temperature 73.4 °F | Parallel; ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 84 | 84 | ASTM D785 | ||
| Tensile Strength at Break | 112 MPa | 16200 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 185 MPa | 26800 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 9.50 GPa | 1380 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm | 266 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C @Thickness 6.40 mm | 244 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |||
| V-2 @Thickness 3.30 mm | V-2 @Thickness 0.130 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 265 °C | <= 509 °F | |||
| Rear Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Start Point: 250°C | ||
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 245°C | ||
| Front Barrel Temperature | 235 - 260 °C | 455 - 500 °F | Start Point: 240°C | ||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | Start Point: 250°C | ||
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | Start Point: 90°C | ||
| Drying Temperature | 100 - 110 °C @Time 7200 - 10800 sec | 212 - 230 °F @Time 2.00 - 3.00 hour | Pre-dry | ||
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi | |||
| Descriptive Properties | |||||
| Injection Speed | 60-80% | ||||