- 熔体流动速率 [g/10min]: 32.0
- 密度 [g/cm3]: 1.75
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in³ | ISO 1183 | ||
| Viscosity Test | 50 cm³/g | 50 cm³/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm | 0.0015 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 32 g/10 min @Load 2.16 kg, Temperature 280 °C | 32 g/10 min @Load 4.76 lb, Temperature 536 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 1.1 % | 1.1 % | ISO 527-1/-2 | ||
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+20 ohm-cm | 2.00e+20 ohm-cm | IEC 60093 | ||
| Surface Resistance | 5.40e+16 ohm | 5.40e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0022 @Frequency 100 Hz | 0.0022 @Frequency 100 Hz | IEC 60250 | ||
| 0.0138 @Frequency 1.00e+6 Hz | 0.0138 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C | 31.1 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| ISO Shortname | ISO7792-PET+PBT,GHMR,07-120,(GF+MD)44 | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.