- 熔体流动速率 [g/10min]: 82.0
- 密度 [g/cm3]: 1.32
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 163.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm | 0.0023 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0023 cm/cm | 0.0023 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 82 g/10 min @Load 2.16 kg, Temperature 250 °C | 82 g/10 min @Load 4.76 lb, Temperature 482 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-1/-2 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | 20 % | 20 % | ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C | 40.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 224 °C | 435 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 48.0 °C | 118 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| Oxygen Index | 28 % | 28 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Flame retarding agent | ||||
| Features | Flame retardant | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GFHMR,09-020; ISO 1043-PBT FR(30+40) | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||