- 密度 [g/cm3]: 1.77
- 缺口冲击强度: 1.01
- 断裂伸长率 [%]: 276
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 - 1.80 g/cc | 0.0639 - 0.0650 lb/in³ | Average value: 1.79 g/cc Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.00200 cm/cm | 0.00100 - 0.00200 in/in | Average value: 0.00167 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 1.50 - 2.00 % | 1.50 - 2.00 % | Average value: 1.67 % Grade Count:3 |
| Flexural Yield Strength | 276 - 303 MPa | 40000 - 44000 psi | Average value: 290 MPa Grade Count:3 |
| Flexural Modulus | 17.2 - 19.3 GPa | 2500 - 2800 ksi | Average value: 18.1 GPa Grade Count:3 |
| Izod Impact, Notched | 1.01 - 1.12 J/cm | 1.90 - 2.10 ft-lb/in | Average value: 1.07 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 - 232 °C | 444 - 450 °F | Average value: 230 °C Grade Count:3 |