- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.12
- 缺口冲击强度: 0.392
- 拉伸强度 [MPa]: 34.0
- 断裂伸长率 [%]: 50.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.14
- 硬度: 108.0
- 热变形温度 [℃]: 79.0
- 透光率 [%]: 0.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 - 1.40 g/cc | 0.0419 - 0.0506 lb/in³ | Average value: 1.21 g/cc Grade Count:119 |
| 1.03 - 1.03 g/cc @Temperature 270 - 270 °C | 0.0372 - 0.0372 lb/in³ @Temperature 518 - 518 °F | Average value: 1.03 g/cc Grade Count:1 | |
| Water Absorption | 0.120 - 0.350 % | 0.120 - 0.350 % | Average value: 0.178 % Grade Count:17 |
| Moisture Absorption at Equilibrium | 0.0100 - 0.700 % | 0.0100 - 0.700 % | Average value: 0.172 % Grade Count:50 |
| Water Absorption at Saturation | 0.0100 - 0.700 % | 0.0100 - 0.700 % | Average value: 0.330 % Grade Count:51 |
| Linear Mold Shrinkage | 0.00150 - 0.0180 cm/cm | 0.00150 - 0.0180 in/in | Average value: 0.00658 cm/cm Grade Count:107 |
| Linear Mold Shrinkage, Transverse | 0.00300 - 0.0100 cm/cm | 0.00300 - 0.0100 in/in | Average value: 0.00600 cm/cm Grade Count:47 |
| Melt Flow | 3.00 - 44.0 g/10 min | 3.00 - 44.0 g/10 min | Average value: 15.6 g/10 min Grade Count:101 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 - 118 | 108 - 118 | Average value: 115 Grade Count:14 |
| Hardness, Shore D | 73.0 - 75.0 | 73.0 - 75.0 | Average value: 73.4 Grade Count:9 |
| Tensile Strength, Ultimate | 35.0 - 110 MPa | 5080 - 16000 psi | Average value: 55.3 MPa Grade Count:79 |
| Tensile Strength, Yield | 34.0 - 70.0 MPa | 4930 - 10200 psi | Average value: 54.1 MPa Grade Count:112 |
| Elongation at Break | 4.00 - 200 % | 4.00 - 200 % | Average value: 128 % Grade Count:97 |
| Elongation at Yield | 2.00 - 86.0 % | 2.00 - 86.0 % | Average value: 6.28 % Grade Count:76 |
| Modulus of Elasticity | 1.16 - 4.15 GPa | 168 - 602 ksi | Average value: 1.98 GPa Grade Count:73 |
| Flexural Yield Strength | 50.0 - 114 MPa | 7250 - 16500 psi | Average value: 81.1 MPa Grade Count:102 |
| Flexural Modulus | 1.14 - 5.10 GPa | 165 - 740 ksi | Average value: 2.05 GPa Grade Count:112 |
| Izod Impact, Notched | 0.392 - 100 J/cm | 0.735 - 187 ft-lb/in | Average value: 7.18 J/cm Grade Count:106 |
| 0.0500 - 7.50 J/cm @Temperature -40.0 - 0.000 °C | 0.0937 - 14.1 ft-lb/in @Temperature -40.0 - 32.0 °F | Average value: 2.33 J/cm Grade Count:51 | |
| 1.60 - 7.50 J/cm @Temperature -40.0 - -22.0 °C | 3.00 - 14.1 ft-lb/in @Temperature -40.0 - -7.60 °F | Average value: 2.33 J/cm Grade Count:5 | |
| 1.60 - 7.50 J/cm @Thickness 3.17 - 3.20 mm | 3.00 - 14.1 ft-lb/in @Thickness 0.125 - 0.126 in | Average value: 2.33 J/cm Grade Count:5 | |
| Izod Impact, Unnotched | 5.88 J/cm - NB | 11.0 ft-lb/in - NB | Average value: 9.91 J/cm Grade Count:8 |
| 99.99 J/cm - NB @Temperature -40.0 - -30.0 °C | 187.3 ft-lb/in - NB @Temperature -40.0 - -22.0 °F | Grade Count:3 | |
| Izod Impact, Notched (ISO) | 7.00 - 78.0 kJ/m² | 3.33 - 37.1 ft-lb/in² | Average value: 20.1 kJ/m² Grade Count:60 |
| 3.00 - 60.0 kJ/m² @Temperature -40.0 - 0.000 °C | 1.43 - 28.6 ft-lb/in² @Temperature -40.0 - 32.0 °F | Average value: 11.6 kJ/m² Grade Count:55 | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² - NB | 47.6 ft-lb/in² - NB | Average value: 105 kJ/m² Grade Count:4 |
| 74.0 kJ/m² - NB @Temperature -30.0 - -30.0 °C | 35.2 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 77.0 kJ/m² Grade Count:4 | |
| Charpy Impact Unnotched | 9.50 J/cm² - NB | 45.2 ft-lb/in² - NB | Average value: 9.50 J/cm² Grade Count:11 |
| 9.50 J/cm² - NB @Temperature -30.0 - -30.0 °C | 45.2 ft-lb/in² - NB @Temperature -22.0 - -22.0 °F | Average value: 9.50 J/cm² Grade Count:11 | |
| Charpy Impact, Notched | 0.600 - 9.00 J/cm² | 2.86 - 42.8 ft-lb/in² | Average value: 3.22 J/cm² Grade Count:61 |
| 0.500 - 5.00 J/cm² @Temperature -30.0 - 0.000 °C | 2.38 - 23.8 ft-lb/in² @Temperature -22.0 - 32.0 °F | Average value: 1.96 J/cm² Grade Count:10 | |
| Gardner Impact | 36.2 J | 26.7 ft-lb | Average value: 36.2 J Grade Count:4 |
| Dart Drop, Total Energy | 5.31 - 95.0 J | 3.92 - 70.1 ft-lb | Average value: 74.9 J Grade Count:46 |
| 5.13856 - 5.13856 J @Temperature -40.0 - -40.0 °C | 3.79000 - 3.79000 ft-lb @Temperature -40.0 - -40.0 °F | Average value: 55.4 J Grade Count:1 | |
| 49.0 - 80.2 J @Temperature -40.0 - 0.000 °C | 36.1 - 59.2 ft-lb @Temperature -40.0 - 32.0 °F | Average value: 55.4 J Grade Count:2 | |
| 49.0 - 80.2 J @Thickness 3.20 - 3.20 mm | 36.1 - 59.2 ft-lb @Thickness 0.126 - 0.126 in | Average value: 55.4 J Grade Count:2 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 12.0 - 1.00e+17 ohm-cm | 12.0 - 1.00e+17 ohm-cm | Average value: 1.98e+16 ohm-cm Grade Count:19 |
| Surface Resistance | 12.0 - 1.00e+15 ohm | 12.0 - 1.00e+15 ohm | Average value: 8.00e+14 ohm Grade Count:15 |
| Static Decay | 2.00 sec | 2.00 sec | Average value: 2.00 sec Grade Count:3 |
| Dielectric Strength | 17.3 - 28.0 kV/mm | 439 - 711 kV/in | Average value: 24.5 kV/mm Grade Count:6 |
| Dissipation Factor | 0.00800 - 0.00900 | 0.00800 - 0.00900 | Average value: 0.00867 Grade Count:3 |
| Arc Resistance | 60.0 - 180 sec | 60.0 - 180 sec | Average value: 121 sec Grade Count:4 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 575 V Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 - 120 µm/m-°C | 22.2 - 66.7 µin/in-°F | Average value: 85.8 µm/m-°C Grade Count:71 |
| CTE, linear, Transverse to Flow | 51.0 - 140 µm/m-°C | 28.3 - 77.8 µin/in-°F | Average value: 87.9 µm/m-°C Grade Count:64 |
| Specific Heat Capacity | 1.34 - 1.76 J/g-°C | 0.320 - 0.421 BTU/lb-°F | Average value: 1.54 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.165 - 0.230 W/m-K | 1.15 - 1.60 BTU-in/hr-ft²-°F | Average value: 0.224 W/m-K Grade Count:16 |
| Melting Point | 220 - 280 °C | 428 - 536 °F | Average value: 246 °C Grade Count:5 |
| Hot Ball Pressure Test | 85.0 - 105 °C | 185 - 221 °F | Average value: 89.4 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 - 255 °C | 174 - 491 °F | Average value: 110 °C Grade Count:77 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.6 - 222 °C | 105 - 432 °F | Average value: 95.5 °C Grade Count:103 |
| Vicat Softening Point | 90.0 - 204 °C | 194 - 399 °F | Average value: 116 °C Grade Count:72 |
| Glass Transition Temp, Tg | 92.0 - 150 °C | 198 - 302 °F | Average value: 115 °C Grade Count:5 |
| UL RTI, Electrical | 75.0 - 105 °C | 167 - 221 °F | Average value: 82.5 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 75.0 - 90.0 °C | 167 - 194 °F | Average value: 78.8 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 75.0 - 105 °C | 167 - 221 °F | Average value: 82.5 °C Grade Count:4 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Average value: 2.00 Grade Count:40 |
| Glow Wire Test | 750 °C | 1380 °F | Average value: 750 °C Grade Count:9 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.54 - 1.58 | 1.54 - 1.58 | Average value: 1.55 Grade Count:12 |
| Haze | 0.500 - 89.0 % | 0.500 - 89.0 % | Average value: 4.80 % Grade Count:43 |
| Transmission, Visible | 0.900 - 90.0 % | 0.900 - 90.0 % | Average value: 83.7 % Grade Count:47 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 282 °C | 446 - 540 °F | Average value: 264 °C Grade Count:8 |
| Nozzle Temperature | 240 - 295 °C | 464 - 563 °F | Average value: 261 °C Grade Count:9 |
| Melt Temperature | 210 - 330 °C | 410 - 626 °F | Average value: 260 °C Grade Count:30 |
| Mold Temperature | 18.0 - 93.3 °C | 64.4 - 200 °F | Average value: 65.8 °C Grade Count:23 |
| Drying Temperature | 88.0 - 127 °C | 190 - 261 °F | Average value: 110 °C Grade Count:18 |
| Dry Time | 3.00 - 8.00 hour | 3.00 - 8.00 hour | Average value: 5.22 hour Grade Count:17 |
| 2.00 - 4.00 hour @Temperature 121 - 121 °C | 2.00 - 4.00 hour @Temperature 250 - 250 °F | Average value: 3.00 hour Grade Count:3 | |
| Moisture Content | 0.000 - 0.0200 % | 0.000 - 0.0200 % | Average value: 0.0142 % Grade Count:6 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:3 |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | Average value: 25.5 l/min Grade Count:3 |
| Injection Pressure | 4.96 - 172 MPa | 720 - 25000 psi | Average value: 55.0 MPa Grade Count:9 |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | Average value: 0.871 MPa Grade Count:10 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:3 |
| Cushion | 0.635 cm | 0.250 in | Average value: 0.635 cm Grade Count:3 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 50.8 rpm Grade Count:10 |