- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.035
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 0.866
- 断裂伸长率 [%]: 177
- 弯曲强度 [MPa]: 72.5
- 弯曲模量 [MPa]: 9.32
- 硬度: 116.0
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 - 1.88 g/cc | 0.0520 - 0.0679 lb/in³ | Average value: 1.71 g/cc Grade Count:21 |
| Water Absorption | 0.0350 - 0.620 % | 0.0350 - 0.620 % | Average value: 0.165 % Grade Count:7 |
| Moisture Absorption at Equilibrium | 0.120 - 0.210 % | 0.120 - 0.210 % | Average value: 0.176 % Grade Count:5 |
| Viscosity | 37000 - 223000 cP @Temperature 285 - 305 °C | 37000 - 223000 cP @Temperature 545 - 581 °F | Average value: 108000 cP Grade Count:1 |
| 37000 - 223000 cP @Shear Rate 500 - 7000 1/s | 37000 - 223000 cP @Shear Rate 500 - 7000 1/s | Average value: 108000 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00100 - 0.00750 cm/cm | 0.00100 - 0.00750 in/in | Average value: 0.00286 cm/cm Grade Count:18 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0115 cm/cm | 0.00500 - 0.0115 in/in | Average value: 0.00783 cm/cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95.0 - 125 | 95.0 - 125 | Average value: 115 Grade Count:5 |
| Hardness, Rockwell R | 116 - 121 | 116 - 121 | Average value: 119 Grade Count:6 |
| Tensile Strength, Ultimate | 72.5 - 210 MPa | 10500 - 30500 psi | Average value: 169 MPa Grade Count:12 |
| 66.9 - 242 MPa @Temperature -40.0 - 150 °C | 9700 - 35100 psi @Temperature -40.0 - 302 °F | Average value: 105 MPa Grade Count:1 | |
| 23.4 - 260 MPa @Temperature -40.0 - 150 °C | 3390 - 37700 psi @Temperature -40.0 - 302 °F | Average value: 105 MPa Grade Count:1 | |
| 23.4 - 260 MPa @Strain 0.190 - 5.19 % | 3390 - 37700 psi @Strain 0.190 - 5.19 % | Average value: 105 MPa Grade Count:1 | |
| Tensile Strength, Yield | 0.866 - 195 MPa | 126 - 28300 psi | Average value: 138 MPa Grade Count:9 |
| Elongation at Break | 1.00 - 6.00 % | 1.00 - 6.00 % | Average value: 2.31 % Grade Count:17 |
| 1.70 - 6.00 % @Temperature -40.0 - 150 °C | 1.70 - 6.00 % @Temperature -40.0 - 302 °F | Average value: 3.55 % Grade Count:1 | |
| Modulus of Elasticity | 15.5 - 19.0 GPa | 2250 - 2760 ksi | Average value: 16.4 GPa Grade Count:9 |
| 5.10 - 16.4 GPa @Temperature -40.0 - 150 °C | 740 - 2380 ksi @Temperature -40.0 - 302 °F | Average value: 11.3 GPa Grade Count:1 | |
| Flexural Yield Strength | 177 - 300 MPa | 25600 - 43500 psi | Average value: 262 MPa Grade Count:14 |
| 96.5 - 370 MPa @Temperature -40.0 - 150 °C | 14000 - 53700 psi @Temperature -40.0 - 302 °F | Average value: 208 MPa Grade Count:2 | |
| Flexural Modulus | 9.32 - 17.0 GPa | 1350 - 2470 ksi | Average value: 13.5 GPa Grade Count:16 |
| 4.00 - 17.9 GPa @Temperature -40.0 - 150 °C | 580 - 2600 ksi @Temperature -40.0 - 302 °F | Average value: 8.11 GPa Grade Count:2 | |
| Shear Modulus | 0.194 - 2.84 GPa @Temperature -50.0 - 250 °C | 28.1 - 412 ksi @Temperature -58.0 - 482 °F | Average value: 1.31 GPa Grade Count:1 |
| Izod Impact, Notched | 0.694 - 1.17 J/cm | 1.30 - 2.19 ft-lb/in | Average value: 0.972 J/cm Grade Count:15 |
| 1.23 - 1.23 J/cm @Temperature -40.0 - -40.0 °C | 2.30 - 2.30 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 1.23 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 0.932 - 10.0 J/cm | 1.75 - 18.7 ft-lb/in | Average value: 7.00 J/cm Grade Count:4 |
| 8.00 - 8.00 J/cm @Temperature -40.0 - -40.0 °C | 15.0 - 15.0 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 8.00 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 9.50 - 13.0 kJ/m² | 4.52 - 6.19 ft-lb/in² | Average value: 10.7 kJ/m² Grade Count:5 |
| 9.00 - 9.00 kJ/m² @Temperature -30.0 - -30.0 °C | 4.28 - 4.28 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 9.00 kJ/m² Grade Count:2 | |
| Charpy Impact Unnotched | 2.40 - 6.00 J/cm² | 11.4 - 28.6 ft-lb/in² | Average value: 4.68 J/cm² Grade Count:5 |
| 2.10 - 5.50 J/cm² @Temperature -30.0 - -30.0 °C | 9.99 - 26.2 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 3.68 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 1.10 - 1.40 J/cm² | 5.24 - 6.66 ft-lb/in² | Average value: 1.17 J/cm² Grade Count:6 |
| 0.900 - 1.40 J/cm² @Temperature -30.0 - -30.0 °C | 4.28 - 6.66 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.18 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 - 1.00e+16 ohm-cm | 1.00e+13 - 1.00e+16 ohm-cm | Average value: 6.17e+15 ohm-cm Grade Count:10 |
| Surface Resistance | 1.00e+14 - 1.00e+15 ohm | 1.00e+14 - 1.00e+15 ohm | Average value: 2.29e+14 ohm Grade Count:6 |
| Dielectric Constant | 3.40 - 5.20 | 3.40 - 5.20 | Average value: 4.00 Grade Count:8 |
| Dielectric Strength | 17.7 - 35.0 kV/mm | 450 - 889 kV/in | Average value: 23.9 kV/mm Grade Count:8 |
| 12.5 - 22.5 kV/mm @Temperature 95.0 - 150 °C | 318 - 572 kV/in @Temperature 203 - 302 °F | Average value: 17.1 kV/mm Grade Count:1 | |
| 12.5 - 22.5 kV/mm @Thickness 1.60 - 3.20 mm | 318 - 572 kV/in @Thickness 0.0630 - 0.126 in | Average value: 17.1 kV/mm Grade Count:1 | |
| Dissipation Factor | 0.00200 - 0.220 | 0.00200 - 0.220 | Average value: 0.0251 Grade Count:7 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | Average value: 225 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.0 - 500 µm/m-°C | 7.78 - 278 µin/in-°F | Average value: 276 µm/m-°C Grade Count:8 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 54.0 - 100 µm/m-°C | 30.0 - 55.6 µin/in-°F | Average value: 74.3 µm/m-°C Grade Count:5 |
| 95.0 - 121 µm/m-°C @Temperature 55.0 - 160 °C | 52.8 - 67.2 µin/in-°F @Temperature 131 - 320 °F | Average value: 104 µm/m-°C Grade Count:2 | |
| Melting Point | 244 - 255 °C | 471 - 491 °F | Average value: 250 °C Grade Count:13 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 - 255 °C | 455 - 491 °F | Average value: 246 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 - 240 °C | 400 - 464 °F | Average value: 226 °C Grade Count:19 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:17 |
| Oxygen Index | 20.0 - 26.0 % | 20.0 - 26.0 % | Average value: 22.0 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 300 °C | 68.0 - 572 °F | Average value: 167 °C Grade Count:5 |
| Feed Temperature | 40.0 - 265 °C | 104 - 509 °F | Average value: 108 °C Grade Count:4 |
| Melt Temperature | 249 - 300 °C | 480 - 572 °F | Average value: 276 °C Grade Count:7 |
| Mold Temperature | 80.0 - 149 °C | 176 - 300 °F | Average value: 114 °C Grade Count:11 |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Average value: 128 °C Grade Count:8 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.86 hour Grade Count:7 |
| Moisture Content | 0.0100 - 0.0800 % | 0.0100 - 0.0800 % | Average value: 0.0329 % Grade Count:7 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 67.0 MPa Grade Count:4 |
| Screw Speed | 50.0 - 100 rpm | 50.0 - 100 rpm | Average value: 66.5 rpm Grade Count:3 |