- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.8
- 断裂伸长率 [%]: 222
- 弯曲模量 [MPa]: 10.69
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.13 % | 0.13 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 86 | 86 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 148.9 MPa | 21600 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 222 MPa | 32200 psi | ASTM D790 |
| Flexural Modulus | 10.69 GPa | 1550 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 @Frequency 60 Hz | 3.7 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 22.7 kV/mm | 577 kV/in | ASTM D149 |
| Arc Resistance | 111 sec | 111 sec | ASTM D495 |
| Comparative Tracking Index | 220 V | 220 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 21.0 µm/m-°C @Temperature 20.0 °C | 11.7 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | RTI |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Vicat Softening Point | >= 225 °C | >= 437 °F | ASTM D1525 |
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | |
| Flammability, UL94 | V-0 | V-0 | 0.028 in |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |