- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 91.0
- 断裂伸长率 [%]: 130
- 弯曲强度 [MPa]: 1.77
- 弯曲模量 [MPa]: 6.30
- 硬度: 109.0
- 热变形温度 [℃]: 94.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 - 1.83 g/cc | 0.0514 - 0.0661 lb/in³ | Average value: 1.61 g/cc Grade Count:46 |
| Filler Content | 35.0 - 40.0 % | 35.0 - 40.0 % | Average value: 36.7 % Grade Count:3 |
| Water Absorption | 0.0300 - 0.830 % | 0.0300 - 0.830 % | Average value: 0.101 % Grade Count:14 |
| Moisture Absorption at Equilibrium | 0.0500 - 0.240 % | 0.0500 - 0.240 % | Average value: 0.157 % Grade Count:7 |
| Viscosity | 30000 - 327000 cP @Temperature 275 - 315 °C | 30000 - 327000 cP @Temperature 527 - 599 °F | Average value: 129000 cP Grade Count:1 |
| 30000 - 327000 cP @Shear Rate 500 - 7000 1/s | 30000 - 327000 cP @Shear Rate 500 - 7000 1/s | Average value: 129000 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00100 - 0.0110 cm/cm | 0.00100 - 0.0110 in/in | Average value: 0.00367 cm/cm Grade Count:32 |
| Linear Mold Shrinkage, Transverse | 0.00530 - 0.0100 cm/cm | 0.00530 - 0.0100 in/in | Average value: 0.00788 cm/cm Grade Count:18 |
| Ash | 25.0 - 35.0 % | 25.0 - 35.0 % | Average value: 31.7 % Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 75.0 - 115 | 75.0 - 115 | Average value: 86.3 Grade Count:5 |
| Hardness, Rockwell R | 109 - 120 | 109 - 120 | Average value: 116 Grade Count:14 |
| Tensile Strength, Ultimate | 1.77 - 152 MPa | 257 - 22000 psi | Average value: 85.3 MPa Grade Count:42 |
| 29.7 - 160 MPa @Temperature -40.0 - 150 °C | 4310 - 23200 psi @Temperature -40.0 - 302 °F | Average value: 39.3 MPa Grade Count:3 | |
| 0.410 - 130.53 MPa @Temperature -40.0 - 150 °C | 59.5 - 18932 psi @Temperature -40.0 - 302 °F | Average value: 39.3 MPa Grade Count:2 | |
| 0.410 - 130.53 MPa @Strain 0.000 - 8.76 % | 59.5 - 18932 psi @Strain 0.000 - 8.76 % | Average value: 39.3 MPa Grade Count:2 | |
| Tensile Strength, Yield | 91.0 - 145 MPa | 13200 - 21000 psi | Average value: 114 MPa Grade Count:4 |
| Elongation at Break | 1.00 - 7.00 % | 1.00 - 7.00 % | Average value: 2.36 % Grade Count:36 |
| 1.60 - 8.10 % @Temperature -40.0 - 150 °C | 1.60 - 8.10 % @Temperature -40.0 - 302 °F | Average value: 4.76 % Grade Count:3 | |
| Modulus of Elasticity | 9.70 - 13.8 GPa | 1410 - 2000 ksi | Average value: 11.6 GPa Grade Count:8 |
| 2.42 - 13.9 GPa @Temperature -40.0 - 150 °C | 351 - 2020 ksi @Temperature -40.0 - 302 °F | Average value: 6.06 GPa Grade Count:3 | |
| Flexural Yield Strength | 130 - 265 MPa | 18900 - 38400 psi | Average value: 182 MPa Grade Count:42 |
| 42.7 - 261 MPa @Temperature -40.0 - 150 °C | 6190 - 37900 psi @Temperature -40.0 - 302 °F | Average value: 111 MPa Grade Count:2 | |
| Flexural Modulus | 6.30 - 15.5 GPa | 914 - 2250 ksi | Average value: 9.68 GPa Grade Count:43 |
| 2.10 - 14.18 GPa @Temperature -40.0 - 150 °C | 305 - 2057 ksi @Temperature -40.0 - 302 °F | Average value: 6.77 GPa Grade Count:2 | |
| Compressive Yield Strength | 126 - 175 MPa | 18300 - 25400 psi | Average value: 148 MPa Grade Count:5 |
| Shear Modulus | 0.0390 - 1.59 GPa @Temperature -50.0 - 250 °C | 5.66 - 231 ksi @Temperature -58.0 - 482 °F | Average value: 0.832 GPa Grade Count:1 |
| Shear Strength | 49.0 - 60.7 MPa | 7110 - 8800 psi | Average value: 55.6 MPa Grade Count:4 |
| Izod Impact, Notched | 0.430 - 0.910 J/cm | 0.806 - 1.70 ft-lb/in | Average value: 0.652 J/cm Grade Count:28 |
| 0.430 - 0.690 J/cm @Temperature -40.0 - -40.0 °C | 0.806 - 1.29 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.560 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 4.25 - 5.34 J/cm | 7.96 - 10.0 ft-lb/in | Average value: 4.83 J/cm Grade Count:8 |
| 2.80 - 4.15 J/cm @Temperature -40.0 - -40.0 °C | 5.25 - 7.77 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 3.47 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 6.00 - 7.00 kJ/m² | 2.86 - 3.33 ft-lb/in² | Average value: 6.51 kJ/m² Grade Count:8 |
| 4.00 - 7.00 kJ/m² @Temperature -40.0 - -30.0 °C | 1.90 - 3.33 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 5.33 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 39.0 - 39.0 kJ/m² @Temperature -40.0 - -40.0 °C | 18.6 - 18.6 ft-lb/in² @Temperature -40.0 - -40.0 °F | Average value: 39.0 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 2.40 - 3.50 J/cm² | 11.4 - 16.7 ft-lb/in² | Average value: 2.75 J/cm² Grade Count:4 |
| 2.00 - 3.50 J/cm² @Temperature -40.0 - -30.0 °C | 9.52 - 16.7 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 2.57 J/cm² Grade Count:3 | |
| Charpy Impact, Notched | 0.320 - 0.860 J/cm² | 1.52 - 4.09 ft-lb/in² | Average value: 0.664 J/cm² Grade Count:18 |
| 0.400 - 0.600 J/cm² @Temperature -40.0 - -30.0 °C | 1.90 - 2.86 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 0.520 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 - 1.00e+17 ohm-cm | 1.00e+15 - 1.00e+17 ohm-cm | Average value: 2.35e+16 ohm-cm Grade Count:23 |
| Surface Resistance | 1.00e+13 - 1.00e+17 ohm | 1.00e+13 - 1.00e+17 ohm | Average value: 5.00e+16 ohm Grade Count:18 |
| Dielectric Constant | 3.50 - 4.50 | 3.50 - 4.50 | Average value: 3.81 Grade Count:8 |
| Dielectric Strength | 16.2 - 39.0 kV/mm | 411 - 991 kV/in | Average value: 22.0 kV/mm Grade Count:26 |
| 10.5 - 25.5 kV/mm @Temperature 95.0 - 150 °C | 267 - 648 kV/in @Temperature 203 - 302 °F | Average value: 16.3 kV/mm Grade Count:2 | |
| 10.5 - 25.5 kV/mm @Thickness 1.60 - 3.20 mm | 267 - 648 kV/in @Thickness 0.0630 - 0.126 in | Average value: 16.3 kV/mm Grade Count:2 | |
| Dissipation Factor | 0.00500 - 0.0300 | 0.00500 - 0.0300 | Average value: 0.0118 Grade Count:7 |
| Arc Resistance | 75.0 - 125 sec | 75.0 - 125 sec | Average value: 94.8 sec Grade Count:4 |
| Comparative Tracking Index | 175 - 400 V | 175 - 400 V | Average value: 230 V Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 17.0 - 500 µm/m-°C | 9.44 - 278 µin/in-°F | Average value: 284 µm/m-°C Grade Count:12 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 30.0 - 87.0 µm/m-°C | 16.7 - 48.3 µin/in-°F | Average value: 58.1 µm/m-°C Grade Count:6 |
| 81.0 - 84.0 µm/m-°C @Temperature 55.0 - 160 °C | 45.0 - 46.7 µin/in-°F @Temperature 131 - 320 °F | Average value: 82.5 µm/m-°C Grade Count:2 | |
| Melting Point | 232 - 268 °C | 450 - 514 °F | Average value: 251 °C Grade Count:19 |
| Maximum Service Temperature, Air | 75.0 - 140 °C | 167 - 284 °F | Average value: 115 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 - 243 °C | 201 - 470 °F | Average value: 225 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 - 242 °C | 174 - 468 °F | Average value: 211 °C Grade Count:45 |
| Vicat Softening Point | 225 °C | 437 °F | Average value: 225 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 128 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:29 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 304 °C | 68.0 - 579 °F | Average value: 236 °C Grade Count:7 |
| Feed Temperature | 50.0 - 270 °C | 122 - 518 °F | Average value: 238 °C Grade Count:8 |
| Nozzle Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 286 °C Grade Count:8 |
| Melt Temperature | 250 - 300 °C | 482 - 572 °F | Average value: 276 °C Grade Count:19 |
| Mold Temperature | 65.0 - 140 °C | 149 - 284 °F | Average value: 106 °C Grade Count:22 |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | Average value: 125 °C Grade Count:8 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.88 hour Grade Count:8 |
| Moisture Content | 0.0100 - 0.0800 % | 0.0100 - 0.0800 % | Average value: 0.0243 % Grade Count:7 |
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | Average value: 72.1 MPa Grade Count:6 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 65.0 MPa Grade Count:3 |