- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.34
- 拉伸强度 [MPa]: 1.06
- 断裂伸长率 [%]: 6.89
- 弯曲强度 [MPa]: 18.2
- 弯曲模量 [MPa]: 2.07
- 硬度: 110.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 - 1.63 g/cc | 0.0499 - 0.0589 lb/in³ | Average value: 1.48 g/cc Grade Count:37 |
| Filler Content | 13.0 - 20.0 % | 13.0 - 20.0 % | Average value: 16.5 % Grade Count:10 |
| Water Absorption | 0.0500 - 2.50 % | 0.0500 - 2.50 % | Average value: 0.316 % Grade Count:14 |
| Moisture Absorption at Equilibrium | 0.100 - 0.250 % | 0.100 - 0.250 % | Average value: 0.200 % Grade Count:11 |
| Viscosity | 47000 - 312000 cP @Temperature 275 - 315 °C | 47000 - 312000 cP @Temperature 527 - 599 °F | Average value: 150000 cP Grade Count:1 |
| 47000 - 312000 cP @Shear Rate 500 - 7000 1/s | 47000 - 312000 cP @Shear Rate 500 - 7000 1/s | Average value: 150000 cP Grade Count:1 | |
| Linear Mold Shrinkage | 0.00150 - 0.0120 cm/cm | 0.00150 - 0.0120 in/in | Average value: 0.00449 cm/cm Grade Count:29 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00868 cm/cm Grade Count:10 |
| Melt Flow | 4.00 - 17.0 g/10 min | 4.00 - 17.0 g/10 min | Average value: 11.3 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 - 123 | 55.0 - 123 | Average value: 95.2 Grade Count:4 |
| Hardness, Rockwell R | 110 - 120 | 110 - 120 | Average value: 115 Grade Count:10 |
| Tensile Strength, Ultimate | 18.2 - 150 MPa | 2640 - 21800 psi | Average value: 92.8 MPa Grade Count:27 |
| 35.9 - 145 MPa @Temperature -40.0 - 150 °C | 5210 - 21000 psi @Temperature -40.0 - 302 °F | Average value: 56.6 MPa Grade Count:2 | |
| 13.4 - 128 MPa @Temperature -20.0 - 150 °C | 1940 - 18600 psi @Temperature -4.00 - 302 °F | Average value: 56.6 MPa Grade Count:1 | |
| 13.4 - 128 MPa @Strain 0.300 - 10.0 % | 1940 - 18600 psi @Strain 0.300 - 10.0 % | Average value: 56.6 MPa Grade Count:1 | |
| Tensile Strength, Yield | 1.06 - 115 MPa | 154 - 16700 psi | Average value: 63.1 MPa Grade Count:10 |
| Elongation at Break | 1.50 - 6.00 % | 1.50 - 6.00 % | Average value: 3.17 % Grade Count:34 |
| 2.00 - 14.0 % @Temperature -40.0 - 150 °C | 2.00 - 14.0 % @Temperature -40.0 - 302 °F | Average value: 8.00 % Grade Count:2 | |
| Modulus of Elasticity | 4.22 - 9.00 GPa | 612 - 1310 ksi | Average value: 6.78 GPa Grade Count:20 |
| 1.69 - 7.721 GPa @Temperature -40.0 - 150 °C | 245 - 1120 ksi @Temperature -40.0 - 302 °F | Average value: 4.25 GPa Grade Count:2 | |
| Flexural Yield Strength | 6.89 - 178 MPa | 1000 - 25900 psi | Average value: 130 MPa Grade Count:23 |
| 34.5 - 210 MPa @Temperature -40.0 - 150 °C | 5000 - 30500 psi @Temperature -40.0 - 302 °F | Average value: 118 MPa Grade Count:2 | |
| Flexural Modulus | 2.07 - 8.10 GPa | 300 - 1170 ksi | Average value: 5.46 GPa Grade Count:26 |
| 1.10 - 6.737 GPa @Temperature -40.0 - 150 °C | 160 - 977.1 ksi @Temperature -40.0 - 302 °F | Average value: 3.33 GPa Grade Count:2 | |
| Compressive Yield Strength | 93.0 - 138 MPa | 13500 - 20000 psi | Average value: 123 MPa Grade Count:3 |
| Izod Impact, Notched | 0.340 - 1.33 J/cm | 0.637 - 2.50 ft-lb/in | Average value: 0.739 J/cm Grade Count:20 |
| 0.690 - 0.690 J/cm @Temperature -40.0 - -40.0 °C | 1.29 - 1.29 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.690 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 2.67 - 8.55 J/cm | 5.00 - 16.0 ft-lb/in | Average value: 4.27 J/cm Grade Count:6 |
| 6.40 - 6.40 J/cm @Temperature -40.0 - -40.0 °C | 12.0 - 12.0 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 6.40 J/cm Grade Count:1 | |
| Izod Impact, Notched (ISO) | 4.50 - 13.0 kJ/m² | 2.14 - 6.19 ft-lb/in² | Average value: 7.64 kJ/m² Grade Count:16 |
| 5.00 - 8.00 kJ/m² @Temperature -40.0 - -30.0 °C | 2.38 - 3.81 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 5.97 kJ/m² Grade Count:9 | |
| Izod Impact, Unnotched (ISO) | 26.0 - 40.0 kJ/m² | 12.4 - 19.0 ft-lb/in² | Average value: 32.0 kJ/m² Grade Count:3 |
| 18.0 - 35.0 kJ/m² @Temperature -40.0 - -30.0 °C | 8.57 - 16.7 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 26.0 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 2.00 - 5.50 J/cm² | 9.52 - 26.2 ft-lb/in² | Average value: 3.71 J/cm² Grade Count:8 |
| 1.50 - 2.50 J/cm² @Temperature -40.0 - 5.00 °C | 7.14 - 11.9 ft-lb/in² @Temperature -40.0 - 41.0 °F | Average value: 2.00 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.470 - 1.10 J/cm² | 2.24 - 5.24 ft-lb/in² | Average value: 0.797 J/cm² Grade Count:10 |
| 0.500 - 0.800 J/cm² @Temperature -40.0 - -30.0 °C | 2.38 - 3.81 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 0.640 J/cm² Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 3.00e+16 ohm-cm | 1.00e+11 - 3.00e+16 ohm-cm | Average value: 7.44e+15 ohm-cm Grade Count:18 |
| Surface Resistance | 1.00e+13 - 1.00e+15 ohm | 1.00e+13 - 1.00e+15 ohm | Average value: 1.72e+14 ohm Grade Count:9 |
| Dielectric Constant | 3.30 - 4.60 | 3.30 - 4.60 | Average value: 3.77 Grade Count:7 |
| Dielectric Strength | 16.1 - 39.0 kV/mm | 410 - 991 kV/in | Average value: 23.1 kV/mm Grade Count:12 |
| 6.50 - 15.5 kV/mm @Temperature 95.0 - 150 °C | 165 - 394 kV/in @Temperature 203 - 302 °F | Average value: 10.4 kV/mm Grade Count:1 | |
| 6.50 - 15.5 kV/mm @Thickness 1.60 - 3.20 mm | 165 - 394 kV/in @Thickness 0.0630 - 0.126 in | Average value: 10.4 kV/mm Grade Count:1 | |
| Dissipation Factor | 0.00300 - 0.0220 | 0.00300 - 0.0220 | Average value: 0.0151 Grade Count:4 |
| Comparative Tracking Index | 175 - 400 V | 175 - 400 V | Average value: 251 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.6 - 500 µm/m-°C | 7.00 - 278 µin/in-°F | Average value: 233 µm/m-°C Grade Count:13 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 70.0 - 130 µm/m-°C | 38.9 - 72.2 µin/in-°F | Average value: 101 µm/m-°C Grade Count:5 |
| 109 - 125 µm/m-°C @Temperature 55.0 - 160 °C | 60.6 - 69.4 µin/in-°F @Temperature 131 - 320 °F | Average value: 114 µm/m-°C Grade Count:2 | |
| Melting Point | 225 - 260 °C | 437 - 500 °F | Average value: 247 °C Grade Count:20 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 - 250 °C | 428 - 482 °F | Average value: 238 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 - 233 °C | 135 - 451 °F | Average value: 203 °C Grade Count:34 |
| UL RTI, Electrical | 75.0 - 140 °C | 167 - 284 °F | Average value: 134 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 123 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 75.0 - 140 °C | 167 - 284 °F | Average value: 134 °C Grade Count:5 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:29 |
| Oxygen Index | 19.0 - 24.0 % | 19.0 - 24.0 % | Average value: 20.5 % Grade Count:3 |
| Glow Wire Test | 675 - 960 °C | 1250 - 1760 °F | Average value: 809 °C Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 293 °C | 68.0 - 560 °F | Average value: 244 °C Grade Count:12 |
| Feed Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Average value: 58.6 °C Grade Count:7 |
| Melt Temperature | 235 - 300 °C | 455 - 572 °F | Average value: 273 °C Grade Count:12 |
| Mold Temperature | 80.0 - 163 °C | 176 - 325 °F | Average value: 117 °C Grade Count:22 |
| Drying Temperature | 116 - 140 °C | 240 - 284 °F | Average value: 126 °C Grade Count:15 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.81 hour Grade Count:16 |
| Moisture Content | 0.0100 - 0.200 % | 0.0100 - 0.200 % | Average value: 0.0673 % Grade Count:15 |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | Average value: 89.6 MPa Grade Count:5 |
| Hold Pressure | 30.0 - 100 MPa | 4350 - 14500 psi | Average value: 74.4 MPa Grade Count:7 |