- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.801
- 断裂伸长率 [%]: 158
- 弯曲强度 [MPa]: 1.89
- 弯曲模量 [MPa]: 7.52
- 硬度: 120.0
- 热变形温度 [℃]: 232.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 - 1.79 g/cc | 0.0535 - 0.0647 lb/in³ | Average value: 1.66 g/cc Grade Count:18 |
| Filler Content | 30.0 - 43.0 % | 30.0 - 43.0 % | Average value: 37.5 % Grade Count:8 |
| Water Absorption | 0.0400 - 0.620 % | 0.0400 - 0.620 % | Average value: 0.250 % Grade Count:10 |
| Moisture Absorption at Equilibrium | 0.120 - 0.240 % | 0.120 - 0.240 % | Average value: 0.180 % Grade Count:5 |
| Linear Mold Shrinkage | 0.000500 - 0.00700 cm/cm | 0.000500 - 0.00700 in/in | Average value: 0.00289 cm/cm Grade Count:11 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0105 cm/cm | 0.00500 - 0.0105 in/in | Average value: 0.00856 cm/cm Grade Count:7 |
| Melt Flow | 6.00 - 70.0 g/10 min | 6.00 - 70.0 g/10 min | Average value: 34.3 g/10 min Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 - 122 | 120 - 122 | Average value: 120 Grade Count:4 |
| Tensile Strength, Ultimate | 1.89 - 207 MPa | 274 - 30000 psi | Average value: 116 MPa Grade Count:16 |
| 55.2 - 210 MPa @Temperature -40.0 - 150 °C | 8010 - 30500 psi @Temperature -40.0 - 302 °F | Average value: 74.2 MPa Grade Count:2 | |
| 0.700 - 221.48 MPa @Temperature -40.0 - 150 °C | 102 - 32123 psi @Temperature -40.0 - 302 °F | Average value: 74.2 MPa Grade Count:2 | |
| 0.700 - 221.48 MPa @Strain 0.000 - 7.82 % | 102 - 32123 psi @Strain 0.000 - 7.82 % | Average value: 74.2 MPa Grade Count:2 | |
| Elongation at Break | 1.00 - 3.60 % | 1.00 - 3.60 % | Average value: 2.21 % Grade Count:14 |
| 1.70 - 6.50 % @Temperature -40.0 - 150 °C | 1.70 - 6.50 % @Temperature -40.0 - 302 °F | Average value: 3.95 % Grade Count:2 | |
| Modulus of Elasticity | 6.90 - 17.0 GPa | 1000 - 2470 ksi | Average value: 13.1 GPa Grade Count:13 |
| 4.38 - 17.1 GPa @Temperature -40.0 - 150 °C | 635 - 2480 ksi @Temperature -40.0 - 302 °F | Average value: 8.92 GPa Grade Count:2 | |
| Flexural Yield Strength | 158 - 305 MPa | 22900 - 44200 psi | Average value: 227 MPa Grade Count:11 |
| 79.3 - 310 MPa @Temperature -40.0 - 150 °C | 11500 - 45000 psi @Temperature -40.0 - 302 °F | Average value: 164 MPa Grade Count:2 | |
| Flexural Modulus | 7.52 - 14.5 GPa | 1090 - 2100 ksi | Average value: 11.1 GPa Grade Count:12 |
| 2.80 - 15.2 GPa @Temperature -40.0 - 150 °C | 406 - 2200 ksi @Temperature -40.0 - 302 °F | Average value: 7.39 GPa Grade Count:2 | |
| Compressive Yield Strength | 172 - 241 MPa | 25000 - 35000 psi | Average value: 204 MPa Grade Count:4 |
| Izod Impact, Notched | 0.801 - 1.28 J/cm | 1.50 - 2.40 ft-lb/in | Average value: 0.954 J/cm Grade Count:10 |
| 0.850 - 1.05 J/cm @Temperature -40.0 - -40.0 °C | 1.59 - 1.97 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.937 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 6.41 - 11.8 J/cm | 12.0 - 22.0 ft-lb/in | Average value: 8.01 J/cm Grade Count:6 |
| 5.10 - 6.40 J/cm @Temperature -40.0 - -40.0 °C | 9.55 - 12.0 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 5.75 J/cm Grade Count:2 | |
| Charpy Impact Unnotched | 4.00 - 7.00 J/cm² | 19.0 - 33.3 ft-lb/in² | Average value: 5.48 J/cm² Grade Count:9 |
| 3.00 - 5.00 J/cm² @Temperature -30.0 - -30.0 °C | 14.3 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.40 J/cm² Grade Count:5 | |
| Charpy Impact, Notched | 0.650 - 1.20 J/cm² | 3.09 - 5.71 ft-lb/in² | Average value: 1.04 J/cm² Grade Count:8 |
| 1.00 - 1.20 J/cm² @Temperature -30.0 - -30.0 °C | 4.76 - 5.71 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.12 J/cm² Grade Count:5 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+14 - 1.00e+17 ohm-cm | 5.00e+14 - 1.00e+17 ohm-cm | Average value: 1.15e+16 ohm-cm Grade Count:10 |
| Surface Resistance | 1.00e+13 - 1.00e+15 ohm | 1.00e+13 - 1.00e+15 ohm | Average value: 6.70e+14 ohm Grade Count:7 |
| Dielectric Constant | 3.10 - 4.20 | 3.10 - 4.20 | Average value: 3.75 Grade Count:8 |
| Dielectric Strength | 17.0 - 34.0 kV/mm | 432 - 864 kV/in | Average value: 25.9 kV/mm Grade Count:10 |
| 12.0 - 23.5 kV/mm @Temperature 95.0 - 200 °C | 305 - 597 kV/in @Temperature 203 - 392 °F | Average value: 18.4 kV/mm Grade Count:2 | |
| 12.0 - 23.5 kV/mm @Thickness 1.57 - 3.20 mm | 305 - 597 kV/in @Thickness 0.0618 - 0.126 in | Average value: 18.4 kV/mm Grade Count:2 | |
| Dissipation Factor | 0.00100 - 0.0170 | 0.00100 - 0.0170 | Average value: 0.00964 Grade Count:7 |
| Comparative Tracking Index | 200 - 400 V | 200 - 400 V | Average value: 253 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 500 µm/m-°C | 11.1 - 278 µin/in-°F | Average value: 342 µm/m-°C Grade Count:10 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:4 | |
| CTE, linear, Transverse to Flow | 55.0 - 85.0 µm/m-°C | 30.6 - 47.2 µin/in-°F | Average value: 69.3 µm/m-°C Grade Count:8 |
| 85.0 - 120 µm/m-°C @Temperature 55.0 - 160 °C | 47.2 - 66.7 µin/in-°F @Temperature 131 - 320 °F | Average value: 99.5 µm/m-°C Grade Count:4 | |
| Melting Point | 254 - 255 °C | 489 - 491 °F | Average value: 255 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 251 °C | 450 - 484 °F | Average value: 245 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 - 248 °C | 392 - 478 °F | Average value: 228 °C Grade Count:17 |
| UL RTI, Electrical | 140 - 155 °C | 284 - 311 °F | Average value: 149 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 140 - 155 °C | 284 - 311 °F | Average value: 149 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 140 - 155 °C | 284 - 311 °F | Average value: 149 °C Grade Count:3 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 243 - 293 °C | 470 - 560 °F | Average value: 268 °C Grade Count:3 |
| Melt Temperature | 246 - 300 °C | 475 - 572 °F | Average value: 273 °C Grade Count:8 |
| Mold Temperature | 91.0 - 163 °C | 196 - 325 °F | Average value: 118 °C Grade Count:10 |
| Drying Temperature | 120 °C | 248 °F | Average value: 120 °C Grade Count:6 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:6 |
| Moisture Content | 0.0100 - 0.0200 % | 0.0100 - 0.0200 % | Average value: 0.0183 % Grade Count:6 |
| Injection Pressure | 55.0 - 103 MPa | 7980 - 15000 psi | Average value: 82.1 MPa Grade Count:4 |