- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.43
- 断裂伸长率 [%]: 171
- 弯曲模量 [MPa]: 10.62
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.11 % | 0.11 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 111.7 MPa | 16200 psi | ASTM D638 |
| Flexural Yield Strength | 171 MPa | 24800 psi | ASTM D790 |
| Flexural Modulus | 10.62 GPa | 1540 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Arc Resistance | 75 sec | 75 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.5 µm/m-°C @Temperature 20.0 °C | 10.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ASTM D648 |
| Vicat Softening Point | >= 225 °C | >= 437 °F | ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 0.125 in; Albis Internal Test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |