- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.1
- 缺口冲击强度: 1.39
- 断裂伸长率 [%]: 131
- 弯曲模量 [MPa]: 3.86
- 硬度: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.24 % | 0.24 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0060 cm/cm | 0.0010 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength at Break | 62.1 MPa | 9010 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 3.86 GPa | 560 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.2 | 3.2 | |
| Dielectric Strength | >= 27.6 kV/mm | >= 701 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 26.0 µm/m-°C @Temperature 20.0 °C | 14.4 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.059 in; Albis Internal test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 277 °C | 500 - 531 °F | Injection |
| Mold Temperature | 74.0 - 93.0 °C | 165 - 199 °F | |