- 密度 [g/cm3]: 1.21
- 缺口冲击强度: 6.83
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 2.00
- 硬度: 108.0
- 热变形温度 [℃]: 131.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 158 % | 158 % | ASTM D638 |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | ASTM D648 |
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 254 - 271 °C | 489 - 520 °F | Approximate middle barrel temperature range |