- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 70.0
- 热变形温度 [℃]: 128.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183-1 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | b.o. ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 110 % | 110 % | 50 mm/min; b.o. ISO 527-1,-2 |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527-1,-2 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 180-A |
| 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180-A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179-1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179-1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eA |
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Vicat Softening Point | 140 °C @Load 5.10 kg | 284 °F @Load 11.2 lb | 120°C/h; ISO 306 |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.10 % | 0.10 % | post-shrinkage; b.o. ISO 2577 |
| Processing Properties | Metric | English | Comments |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |