- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 0.16
- 缺口冲击强度: 7.5
- 拉伸强度 [MPa]: 55.2
- 断裂伸长率 [%]: 90.0
- 弯曲强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 2.41
- 硬度: 117.0
- 热变形温度 [℃]: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.16 % | 0.16 % | 24 hour immersion; ASTM D570 |
| Water Absorption at Saturation | 0.34 % | 0.34 % | Equilibrium Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 20 - 30 g/10 min @Load 5.00 kg, Temperature 265 °C | 20 - 30 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
| Tensile Strength, Yield | 55.2 MPa | 8010 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm @Thickness 3.17 mm | 14.1 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 1.60 J/cm @Thickness 3.17 mm, Temperature -29.0 °C | 3.00 ft-lb/in @Thickness 0.125 in, Temperature -20.2 °F | ASTM D256 | |
| Impact Test | 50.0 J @Thickness 3.20 mm | 36.9 ft-lb @Thickness 0.126 in | Instrumented Impact, Total Energy; 3.2 mm thick, 15 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 60 - 120 sec @Thickness 3.00 mm | 60 - 120 sec @Thickness 0.118 in | UL Rating PLC 6 (60-120 sec) |
| Comparative Tracking Index | 250 - 400 V @Thickness 3.00 mm | 250 - 400 V @Thickness 0.118 in | UL Rating PLC 2 (250-400 V) |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 3.00 mm | 60 - 120 sec @Thickness 0.118 in | UL Rating PLC 1 (60-120 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 1.50 mm | >= 120 arcs @Thickness 0.0591 in | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min @Thickness 3.00 mm | >= 5.91 in/min @Thickness 0.118 in | UL Rating PLC 4 (>150 mm/min.) |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 6.40 mm | 246 °F @Thickness 0.252 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.35 mm | 212 °F @Thickness 0.250 in | ASTM D648 |
| UL RTI, Electrical | 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | UL746B |
| UL RTI, Mechanical with Impact | 90.0 °C @Thickness 1.50 mm | 194 °F @Thickness 0.0591 in | UL746B |
| UL RTI, Mechanical without Impact | 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | UL746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 277 °C | 500 - 531 °F | |