DuPont Performance Polymers Rynite® 545 NC010 PET

DuPont Performance Polymers Rynite® 545 NC010 PET 物性表: DuPont Performance Polymers Rynite® 545 NC010 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 545 NC010 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 545 NC010 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.69
  • 吸水率 [%]: 0.04
  • 成型收缩率 [%]: 0.0015
  • 缺口冲击强度: 1.17
  • 弯曲模量 [MPa]: 4.00
  • 硬度: 120.0
  • 热变形温度 [℃]: 248.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.70 g/cc1.70 g/ccASTM D792
Density 1.69 g/cc0.0611 lb/in³ISO 1183
Filler Content 45 %45 %
Water Absorption  0.040 %
@Temperature 23.0 °C		0.040 %
@Temperature 73.4 °F		50%RH,23°C,24h; ASTM D570
 0.14 %
@Temperature 23.0 °C		0.14 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.62 %
@Temperature 23.0 °C		0.62 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  37000 cP
@Shear Rate 7000 1/s,
Temperature 305 °C		37000 cP
@Shear Rate 7000 1/s,
Temperature 581 °F		ISO 11443
 43000 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		43000 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		ISO 11443
 47000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		47000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		ISO 11443
 55000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		55000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		ISO 11443
 60000 cP
@Shear Rate 7000 1/s,
Temperature 285 °C		60000 cP
@Shear Rate 7000 1/s,
Temperature 545 °F		ISO 11443
 69000 cP
@Shear Rate 2000 1/s,
Temperature 305 °C		69000 cP
@Shear Rate 2000 1/s,
Temperature 581 °F		ISO 11443
 70000 cP
@Shear Rate 5000 1/s,
Temperature 285 °C		70000 cP
@Shear Rate 5000 1/s,
Temperature 545 °F		ISO 11443
 88000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		88000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		ISO 11443
 98000 cP
@Shear Rate 1000 1/s,
Temperature 305 °C		98000 cP
@Shear Rate 1000 1/s,
Temperature 581 °F		ISO 11443
 111000 cP
@Shear Rate 2000 1/s,
Temperature 285 °C		111000 cP
@Shear Rate 2000 1/s,
Temperature 545 °F		ISO 11443
 117000 cP
@Shear Rate 700 1/s,
Temperature 305 °C		117000 cP
@Shear Rate 700 1/s,
Temperature 581 °F		ISO 11443
 124000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		124000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		ISO 11443
 139000 cP
@Shear Rate 500 1/s,
Temperature 305 °C		139000 cP
@Shear Rate 500 1/s,
Temperature 581 °F		ISO 11443
 148000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		148000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		ISO 11443
 157000 cP
@Shear Rate 1000 1/s,
Temperature 285 °C		157000 cP
@Shear Rate 1000 1/s,
Temperature 545 °F		ISO 11443
 175000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		175000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		ISO 11443
 189000 cP
@Shear Rate 700 1/s,
Temperature 285 °C		189000 cP
@Shear Rate 700 1/s,
Temperature 545 °F		ISO 11443
 223000 cP
@Shear Rate 500 1/s,
Temperature 285 °C		223000 cP
@Shear Rate 500 1/s,
Temperature 545 °F		ISO 11443
Linear Mold Shrinkage  0.0015 cm/cm
@Thickness 1.57 mm		0.0015 in/in
@Thickness 0.0618 in		Flow
 0.0020 cm/cm
@Thickness 3.20 mm		0.0020 in/in
@Thickness 0.126 in		Flow
 0.0067 cm/cm
@Thickness 1.57 mm		0.0067 in/in
@Thickness 0.0618 in		Transverse
 0.0075 cm/cm
@Thickness 3.20 mm		0.0075 in/in
@Thickness 0.126 in		Transverse
Linear Mold Shrinkage, Flow 0.0030 cm/cm0.0030 in/inParallel; Annealed; ISO 294-4
 0.0025 cm/cm
@Thickness 2.00 mm		0.0025 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0115 cm/cm0.0115 in/inNormal; Annealed; ISO 294-4
 0.0085 cm/cm
@Thickness 2.00 mm		0.0085 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 2.5 g/10 min
@Load 2.16 kg,
Temperature 280 °C		2.5 g/10 min
@Load 4.76 lb,
Temperature 536 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 9595ASTM D785
 100100ISO 2039/2
Hardness, Rockwell R 120120ASTM D785
 120120ISO 2039/2
Tensile Strength at Break  182 MPa
@Temperature 23.0 °C		26400 psi
@Temperature 73.4 °F		ISO 527
 233 MPa
@Temperature -40.0 °C		33800 psi
@Temperature -40.0 °F		ISO 527
Tensile Strength  66.9 MPa
@Temperature 150 °C		9700 psi
@Temperature 302 °F		ASTM D638
 91.7 MPa
@Temperature 90.0 °C		13300 psi
@Temperature 194 °F		ASTM D638
 186 MPa
@Temperature 23.0 °C		27000 psi
@Temperature 73.4 °F		ASTM D638
 242 MPa
@Temperature -40.0 °C		35100 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  23.4 MPa
@Strain 0.520 %,
Temperature 150 °C		3390 psi
@Strain 0.520 %,
Temperature 302 °F		ISO 527
 27.5 MPa
@Strain 0.450 %,
Temperature 120 °C		3990 psi
@Strain 0.450 %,
Temperature 248 °F		ISO 527
 30.7 MPa
@Strain 0.460 %,
Temperature 90.0 °C		4450 psi
@Strain 0.460 %,
Temperature 194 °F		ISO 527
 34.7 MPa
@Strain 0.190 %,
Temperature 0.000 °C		5030 psi
@Strain 0.190 %,
Temperature 32.0 °F		ISO 527
 35.0 MPa
@Strain 0.220 %,
Temperature 40.0 °C		5080 psi
@Strain 0.220 %,
Temperature 104 °F		ISO 527
 36.2 MPa
@Strain 0.320 %,
Temperature 60.0 °C		5250 psi
@Strain 0.320 %,
Temperature 140 °F		ISO 527
 37.3 MPa
@Strain 1.03 %,
Temperature 150 °C		5410 psi
@Strain 1.03 %,
Temperature 302 °F		ISO 527
 37.6 MPa
@Strain 0.200 %,
Temperature -40.0 °C		5450 psi
@Strain 0.200 %,
Temperature -40.0 °F		ISO 527
 43.6 MPa
@Strain 0.900 %,
Temperature 120 °C		6320 psi
@Strain 0.900 %,
Temperature 248 °F		ISO 527
 45.2 MPa
@Strain 1.56 %,
Temperature 150 °C		6560 psi
@Strain 1.56 %,
Temperature 302 °F		ISO 527
 50.7 MPa
@Strain 2.07 %,
Temperature 150 °C		7350 psi
@Strain 2.07 %,
Temperature 302 °F		ISO 527
 52.0 MPa
@Strain 0.920 %,
Temperature 90.0 °C		7540 psi
@Strain 0.920 %,
Temperature 194 °F		ISO 527
 54.3 MPa
@Strain 1.35 %,
Temperature 120 °C		7880 psi
@Strain 1.35 %,
Temperature 248 °F		ISO 527
 54.9 MPa
@Strain 2.59 %,
Temperature 150 °C		7960 psi
@Strain 2.59 %,
Temperature 302 °F		ISO 527
 58.4 MPa
@Strain 3.11 %,
Temperature 150 °C		8470 psi
@Strain 3.11 %,
Temperature 302 °F		ISO 527
 61.3 MPa
@Strain 3.63 %,
Temperature 150 °C		8890 psi
@Strain 3.63 %,
Temperature 302 °F		ISO 527
 61.6 MPa
@Strain 1.80 %,
Temperature 120 °C		8930 psi
@Strain 1.80 %,
Temperature 248 °F		ISO 527
 63.5 MPa
@Strain 4.12 %,
Temperature 150 °C		9210 psi
@Strain 4.12 %,
Temperature 302 °F		ISO 527
 64.5 MPa
@Strain 0.450 %,
Temperature 40.0 °C		9350 psi
@Strain 0.450 %,
Temperature 104 °F		ISO 527
 64.7 MPa
@Strain 0.640 %,
Temperature 60.0 °C		9380 psi
@Strain 0.640 %,
Temperature 140 °F		ISO 527
 65.6 MPa
@Strain 4.67 %,
Temperature 150 °C		9510 psi
@Strain 4.67 %,
Temperature 302 °F		ISO 527
 65.8 MPa
@Strain 0.380 %,
Temperature 0.000 °C		9540 psi
@Strain 0.380 %,
Temperature 32.0 °F		ISO 527
 66.1 MPa
@Strain 1.38 %,
Temperature 90.0 °C		9590 psi
@Strain 1.38 %,
Temperature 194 °F		ISO 527
 67.0 MPa
@Strain 2.25 %,
Temperature 120 °C		9720 psi
@Strain 2.25 %,
Temperature 248 °F		ISO 527
 68.5 MPa
@Strain 5.19 %,
Temperature 150 °C		9940 psi
@Strain 5.19 %,
Temperature 302 °F		ISO 527
 71.2 MPa
@Strain 2.71 %,
Temperature 120 °C		10300 psi
@Strain 2.71 %,
Temperature 248 °F		ISO 527
 72.3 MPa
@Strain 0.400 %,
Temperature -40.0 °C		10500 psi
@Strain 0.400 %,
Temperature -40.0 °F		ISO 527
 72.5 MPa
@Strain 0.500 %,
Temperature 23.0 °C		10500 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 74.6 MPa
@Strain 3.16 %,
Temperature 120 °C		10800 psi
@Strain 3.16 %,
Temperature 248 °F		ISO 527
 75.6 MPa
@Strain 1.84 %,
Temperature 90.0 °C		11000 psi
@Strain 1.84 %,
Temperature 194 °F		ISO 527
 77.4 MPa
@Strain 3.61 %,
Temperature 120 °C		11200 psi
@Strain 3.61 %,
Temperature 248 °F		ISO 527
 79.7 MPa
@Strain 4.06 %,
Temperature 120 °C		11600 psi
@Strain 4.06 %,
Temperature 248 °F		ISO 527
 81.7 MPa
@Strain 4.51 %,
Temperature 120 °C		11800 psi
@Strain 4.51 %,
Temperature 248 °F		ISO 527
 82.6 MPa
@Strain 2.30 %,
Temperature 90.0 °C		12000 psi
@Strain 2.30 %,
Temperature 194 °F		ISO 527
 86.6 MPa
@Strain 0.970 %,
Temperature 60.0 °C		12600 psi
@Strain 0.970 %,
Temperature 140 °F		ISO 527
 87.9 MPa
@Strain 2.76 %,
Temperature 90.0 °C		12700 psi
@Strain 2.76 %,
Temperature 194 °F		ISO 527
 90.1 MPa
@Strain 0.670 %,
Temperature 40.0 °C		13100 psi
@Strain 0.670 %,
Temperature 104 °F		ISO 527
 92.0 MPa
@Strain 3.22 %,
Temperature 90.0 °C		13300 psi
@Strain 3.22 %,
Temperature 194 °F		ISO 527
 94.4 MPa
@Strain 0.570 %,
Temperature 0.000 °C		13700 psi
@Strain 0.570 %,
Temperature 32.0 °F		ISO 527
 95.2 MPa
@Strain 3.68 %,
Temperature 90.0 °C		13800 psi
@Strain 3.68 %,
Temperature 194 °F		ISO 527
 97.8 MPa
@Strain 4.14 %,
Temperature 90.0 °C		14200 psi
@Strain 4.14 %,
Temperature 194 °F		ISO 527
 99.5 MPa
@Strain 4.61 %,
Temperature 90.0 °C		14400 psi
@Strain 4.61 %,
Temperature 194 °F		ISO 527
 101.6 MPa
@Strain 1.28 %,
Temperature 60.0 °C		14740 psi
@Strain 1.28 %,
Temperature 140 °F		ISO 527
 105 MPa
@Strain 0.610 %,
Temperature -40.0 °C		15200 psi
@Strain 0.610 %,
Temperature -40.0 °F		ISO 527
 110 MPa
@Strain 0.900 %,
Temperature 40.0 °C		16000 psi
@Strain 0.900 %,
Temperature 104 °F		ISO 527
 112.4 MPa
@Strain 1.61 %,
Temperature 60.0 °C		16300 psi
@Strain 1.61 %,
Temperature 140 °F		ISO 527
 120 MPa
@Strain 0.760 %,
Temperature 0.000 °C		17400 psi
@Strain 0.760 %,
Temperature 32.0 °F		ISO 527
 120.1 MPa
@Strain 1.93 %,
Temperature 60.0 °C		17420 psi
@Strain 1.93 %,
Temperature 140 °F		ISO 527
 125.6 MPa
@Strain 2.25 %,
Temperature 60.0 °C		18220 psi
@Strain 2.25 %,
Temperature 140 °F		ISO 527
 126 MPa
@Strain 1.12 %,
Temperature 40.0 °C		18300 psi
@Strain 1.12 %,
Temperature 104 °F		ISO 527
 126 MPa
@Strain 1.00 %,
Temperature 23.0 °C		18300 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 129.3 MPa
@Strain 2.58 %,
Temperature 60.0 °C		18750 psi
@Strain 2.58 %,
Temperature 140 °F		ISO 527
 131.9 MPa
@Strain 2.90 %,
Temperature 60.0 °C		19130 psi
@Strain 2.90 %,
Temperature 140 °F		ISO 527
 133.5 MPa
@Strain 3.22 %,
Temperature 60.0 °C		19360 psi
@Strain 3.22 %,
Temperature 140 °F		ISO 527
 135 MPa
@Strain 0.810 %,
Temperature -40.0 °C		19600 psi
@Strain 0.810 %,
Temperature -40.0 °F		ISO 527
 138 MPa
@Strain 1.34 %,
Temperature 40.0 °C		20000 psi
@Strain 1.34 %,
Temperature 104 °F		ISO 527
 143 MPa
@Strain 0.950 %,
Temperature 0.000 °C		20700 psi
@Strain 0.950 %,
Temperature 32.0 °F		ISO 527
 147 MPa
@Strain 1.57 %,
Temperature 40.0 °C		21300 psi
@Strain 1.57 %,
Temperature 104 °F		ISO 527
 154 MPa
@Strain 1.79 %,
Temperature 40.0 °C		22300 psi
@Strain 1.79 %,
Temperature 104 °F		ISO 527
 159 MPa
@Strain 2.02 %,
Temperature 40.0 °C		23100 psi
@Strain 2.02 %,
Temperature 104 °F		ISO 527
 162 MPa
@Strain 2.24 %,
Temperature 40.0 °C		23500 psi
@Strain 2.24 %,
Temperature 104 °F		ISO 527
 162 MPa
@Strain 1.01 %,
Temperature -40.0 °C		23500 psi
@Strain 1.01 %,
Temperature -40.0 °F		ISO 527
 162 MPa
@Strain 1.14 %,
Temperature 0.000 °C		23500 psi
@Strain 1.14 %,
Temperature 32.0 °F		ISO 527
 163 MPa
@Strain 1.50 %,
Temperature 23.0 °C		23600 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 175 MPa
@Strain 2.00 %,
Temperature 23.0 °C		25400 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 179 MPa
@Strain 1.33 %,
Temperature 0.000 °C		26000 psi
@Strain 1.33 %,
Temperature 32.0 °F		ISO 527
 187 MPa
@Strain 1.21 %,
Temperature -40.0 °C		27100 psi
@Strain 1.21 %,
Temperature -40.0 °F		ISO 527
 193 MPa
@Strain 1.52 %,
Temperature 0.000 °C		28000 psi
@Strain 1.52 %,
Temperature 32.0 °F		ISO 527
 200 MPa
@Strain 2.50 %,
Temperature 23.0 °C		29000 psi
@Strain 2.50 %,
Temperature 73.4 °F		Break; ISO 527
 204 MPa
@Strain 1.71 %,
Temperature 0.000 °C		29600 psi
@Strain 1.71 %,
Temperature 32.0 °F		ISO 527
 209 MPa
@Strain 1.41 %,
Temperature -40.0 °C		30300 psi
@Strain 1.41 %,
Temperature -40.0 °F		ISO 527
 213 MPa
@Strain 1.90 %,
Temperature 0.000 °C		30900 psi
@Strain 1.90 %,
Temperature 32.0 °F		ISO 527
 228 MPa
@Strain 1.61 %,
Temperature -40.0 °C		33100 psi
@Strain 1.61 %,
Temperature -40.0 °F		ISO 527
 246 MPa
@Strain 1.82 %,
Temperature -40.0 °C		35700 psi
@Strain 1.82 %,
Temperature -40.0 °F		ISO 527
 260 MPa
@Strain 2.02 %,
Temperature -40.0 °C		37700 psi
@Strain 2.02 %,
Temperature -40.0 °F		ISO 527
Elongation at Break  1.7 %
@Temperature -40.0 °C		1.7 %
@Temperature -40.0 °F		ASTM D638
 2.0 %
@Temperature -40.0 °C		2.0 %
@Temperature -40.0 °F		ISO 527
 2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		ISO 527
 2.1 %
@Temperature 23.0 °C		2.1 %
@Temperature 73.4 °F		ASTM D638
 4.5 %
@Temperature 90.0 °C		4.5 %
@Temperature 194 °F		ASTM D638
 6.0 %
@Temperature 150 °C		6.0 %
@Temperature 302 °F		ASTM D638
Tensile Modulus  5.10 GPa
@Temperature 150 °C		740 ksi
@Temperature 302 °F		ASTM D638
 8.41 GPa
@Temperature 90.0 °C		1220 ksi
@Temperature 194 °F		ASTM D638
 15.255 GPa
@Temperature -40.0 °C		2212.6 ksi
@Temperature -40.0 °F		ISO 527
 15.5 GPa
@Temperature 23.0 °C		2250 ksi
@Temperature 73.4 °F		ASTM D638
 15.5 GPa
@Temperature 23.0 °C		2250 ksi
@Temperature 73.4 °F		ISO 527
 16.4 GPa
@Temperature -40.0 °C		2380 ksi
@Temperature -40.0 °F		ASTM D638
Flexural Strength  96.5 MPa
@Temperature 150 °C		14000 psi
@Temperature 302 °F		ASTM D790
 141 MPa
@Temperature 90.0 °C		20500 psi
@Temperature 194 °F		ASTM D790
 283 MPa
@Temperature 23.0 °C		41000 psi
@Temperature 73.4 °F		ASTM D790
 324 MPa
@Temperature -40.0 °C		47000 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  4.00 GPa
@Temperature 150 °C		580 ksi
@Temperature 302 °F		ASTM D790
 4.00 GPa
@Temperature 150 °C		580 ksi
@Temperature 302 °F		ISO 178
 5.50 GPa
@Temperature 93.0 °C		798 ksi
@Temperature 199 °F		ISO 178
 5.51 GPa
@Temperature 90.0 °C		799 ksi
@Temperature 194 °F		ASTM D790
 13.5 GPa
@Temperature 23.0 °C		1960 ksi
@Temperature 73.4 °F		ISO 178
 15.2 GPa
@Temperature 23.0 °C		2200 ksi
@Temperature 73.4 °F		ASTM D790
 15.2 GPa
@Temperature -40.0 °C		2200 ksi
@Temperature -40.0 °F		ISO 178
 17.9 GPa
@Temperature -40.0 °C		2600 ksi
@Temperature -40.0 °F		ASTM D790
Compressive Strength 235 MPa
@Temperature 23.0 °C		34100 psi
@Temperature 73.4 °F		ASTM D695
Shear Modulus  0.194 GPa
@Temperature 250 °C		28.1 ksi
@Temperature 482 °F		ISO 6721
 0.304 GPa
@Temperature 240 °C		44.1 ksi
@Temperature 464 °F		ISO 6721
 0.377 GPa
@Temperature 230 °C		54.7 ksi
@Temperature 446 °F		ISO 6721
 0.427 GPa
@Temperature 220 °C		61.9 ksi
@Temperature 428 °F		ISO 6721
 0.468 GPa
@Temperature 210 °C		67.9 ksi
@Temperature 410 °F		ISO 6721
 0.497 GPa
@Temperature 200 °C		72.1 ksi
@Temperature 392 °F		ISO 6721
 0.516 GPa
@Temperature 190 °C		74.8 ksi
@Temperature 374 °F		ISO 6721
 0.534 GPa
@Temperature 180 °C		77.5 ksi
@Temperature 356 °F		ISO 6721
 0.549 GPa
@Temperature 170 °C		79.6 ksi
@Temperature 338 °F		ISO 6721
 0.564 GPa
@Temperature 160 °C		81.8 ksi
@Temperature 320 °F		ISO 6721
 0.578 GPa
@Temperature 150 °C		83.8 ksi
@Temperature 302 °F		ISO 6721
 0.594 GPa
@Temperature 140 °C		86.2 ksi
@Temperature 284 °F		ISO 6721
 0.615 GPa
@Temperature 130 °C		89.2 ksi
@Temperature 266 °F		ISO 6721
 0.645 GPa
@Temperature 120 °C		93.6 ksi
@Temperature 248 °F		ISO 6721
 0.761 GPa
@Temperature 100 °C		110 ksi
@Temperature 212 °F		ISO 6721
 0.761 GPa
@Temperature 110 °C		110 ksi
@Temperature 230 °F		ISO 6721
 0.839 GPa
@Temperature 90.0 °C		122 ksi
@Temperature 194 °F		ISO 6721
 0.976 GPa
@Temperature 80.0 °C		142 ksi
@Temperature 176 °F		ISO 6721
 1.35 GPa
@Temperature 70.0 °C		196 ksi
@Temperature 158 °F		ISO 6721
 1.83 GPa
@Temperature 60.0 °C		265 ksi
@Temperature 140 °F		ISO 6721
 2.27 GPa
@Temperature 50.0 °C		329 ksi
@Temperature 122 °F		ISO 6721
 2.39 GPa
@Temperature 40.0 °C		347 ksi
@Temperature 104 °F		ISO 6721
 2.44 GPa
@Temperature 30.0 °C		354 ksi
@Temperature 86.0 °F		ISO 6721
 2.49 GPa
@Temperature 20.0 °C		361 ksi
@Temperature 68.0 °F		ISO 6721
 2.54 GPa
@Temperature 10.0 °C		368 ksi
@Temperature 50.0 °F		ISO 6721
 2.58 GPa
@Temperature 0.000 °C		374 ksi
@Temperature 32.0 °F		ISO 6721
 2.63 GPa
@Temperature -10.0 °C		381 ksi
@Temperature 14.0 °F		ISO 6721
 2.68 GPa
@Temperature -20.0 °C		389 ksi
@Temperature -4.00 °F		ISO 6721
 2.73 GPa
@Temperature -30.0 °C		396 ksi
@Temperature -22.0 °F		ISO 6721
 2.78 GPa
@Temperature -40.0 °C		403 ksi
@Temperature -40.0 °F		ISO 6721
 2.84 GPa
@Temperature -50.0 °C		412 ksi
@Temperature -58.0 °F		ISO 6721
Shear Strength 86.5 MPa
@Temperature 23.0 °C		12500 psi
@Temperature 73.4 °F		ASTM D732
Izod Impact, Notched  1.17 J/cm
@Temperature 23.0 °C		2.19 ft-lb/in
@Temperature 73.4 °F		ASTM D256
 1.23 J/cm
@Temperature -40.0 °C		2.30 ft-lb/in
@Temperature -40.0 °F		ASTM D256
Izod Impact, Unnotched  8.00 J/cm
@Temperature -40.0 °C		15.0 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 10.0 J/cm
@Temperature 23.0 °C		18.7 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.10 J/cm²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 15600 MPa
@Temperature 23.0 °C		2.26e+6 psi
@Temperature 73.4 °F		ISO 899
Tensile Creep Modulus, 1000 hours 13300 MPa
@Temperature 23.0 °C		1.93e+6 psi
@Temperature 73.4 °F		ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance  1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.9
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.9
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 4.0
@Frequency 1000 Hz,
Temperature 23.0 °C		4.0
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.4
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.4
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 4.5
@Frequency 100 Hz,
Temperature 23.0 °C		4.5
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  12.5 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		318 kV/in
@Thickness 0.126 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 16.0 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		406 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 17.5 kV/mm
@Thickness 3.20 mm,
Temperature 95.0 °C		445 kV/in
@Thickness 0.126 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 20.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		508 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 22.5 kV/mm
@Thickness 1.60 mm,
Temperature 95.0 °C		572 kV/in
@Thickness 0.0630 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 24.5 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		622 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 32.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		813 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
Dissipation Factor  0.0050
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0050
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.0070
@Frequency 100 Hz,
Temperature 23.0 °C		0.0070
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.011
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.011
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.011
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.011
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index 250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		IEC 60112
 >= 200 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 200 V
@Thickness 0.118 in,
Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  54.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		30.0 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 54.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		30.0 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 71.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		39.4 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 71.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		39.4 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 95.0 µm/m-°C
@Temperature 55.0 - 160 °C		52.8 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 95.0 µm/m-°C
@Temperature 55.0 - 160 °C		52.8 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 84.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		46.7 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 84.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		46.7 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 254 °C489 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 248 °C478 °FASTM D648
 250 °C482 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 226 °C439 °FISO 75-1/-2
 226 °C439 °FASTM D648
Deflection Temperature at 8.0 MPa 180 °C356 °FISO 75-1/-2
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 0.810 mm		284 °F
@Thickness 0.0319 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical with Impact  140 °C
@Thickness 0.810 mm		284 °F
@Thickness 0.0319 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 0.810 mm		284 °F
@Thickness 0.0319 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
Oxygen Index 20 %20 %ASTM D2863
 20 %20 %ISO 4589-1/-2
Glow Wire Test  750 °C
@Thickness 2.00 mm		1380 °F
@Thickness 0.0787 in		IEC 60695-2-12
 850 °C
@Thickness 3.00 mm		1560 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 252 °C486 °F10°C/min; ISO 11357-1/-3
 285 °C545 °FOptimum
 280 - 300 °C536 - 572 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AppearanceNatural Color
Drying RecommendedYes
FeaturesCreep Resistance, Good
 Dimensional Stability, Good
 Electrical Properties, Good
 Stiffness, Good
 Strength, Good
 Thermal Aging Resistance, Good
FillerGlass fiber reinforcement
FormsPellets
GenericPET
Heat StabilizedYes
Material StatusPreliminary Data
Part Marking Code>PET-GF45<ISO 11469
Polymer FamilyPolyester
Polymer TypePET
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPET-GF45ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Electrical/Electronic Applications
 Housings
 Phenolic Replacement
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38918.html

免责声明: 本文 DuPont Performance Polymers Rynite® 545 NC010 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4