- 熔体流动速率 [g/10min]: 8.47
- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.35
- 缺口冲击强度: 40.0
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 2.20
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.35 % | 0.35 % | Sim. to ISO 62 | ||
| Melt Flow | 8.47 g/10 min @Load 1.20 kg, Temperature 280 °C | 8.47 g/10 min @Load 2.65 lb, Temperature 536 °F | Calculated from Volume Flow Rate of 7 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 40.0 kJ/m² @Temperature -40.0 °C | 19.0 ft-lb/in² @Temperature -40.0 °F | ISO 180/4A | ||
| 60.0 kJ/m² @Temperature -20.0 °C | 28.6 ft-lb/in² @Temperature -4.00 °F | ISO 180/4A | |||
| 70.0 kJ/m² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 180/4A | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.50 J/cm² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 125 °C | 257 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| High Impact or Impact Modified | Yes | ||||
| Injection Molding | Yes | ||||
| Without Fillers | Yes | ||||