DuPont Performance Polymers Rynite® FR543 NC010 PET

DuPont Performance Polymers Rynite® FR543 NC010 PET 物性表: DuPont Performance Polymers Rynite® FR543 NC010 PET物性表及特性介绍,DuPont Performance Polymers Rynite® FR543 NC010 PET注塑参数详情,如需DuPont Performance Polymers Rynite® FR543 NC010 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.79
  • 吸水率 [%]: 0.06
  • 成型收缩率 [%]: 0.0013
  • 缺口冲击强度: 0.91
  • 弯曲模量 [MPa]: 2.90
  • 硬度: 120.0
  • 热变形温度 [℃]: 240.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.79 g/cc1.79 g/ccASTM D792
Density 1.79 g/cc0.0647 lb/in³ISO 1183
Filler Content 43 %43 %
Water Absorption  0.060 %
@Temperature 23.0 °C
0.060 %
@Temperature 73.4 °F
50%RH,23°C,24h; ASTM D570
 0.11 %
@Temperature 23.0 °C
0.11 %
@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
 0.62 %
@Temperature 23.0 °C
0.62 %
@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage  0.0013 cm/cm
@Thickness 1.57 mm
0.0013 in/in
@Thickness 0.0618 in
Flow
 0.0020 cm/cm
@Thickness 3.20 mm
0.0020 in/in
@Thickness 0.126 in
Flow
 0.0048 cm/cm
@Thickness 1.57 mm
0.0048 in/in
@Thickness 0.0618 in
Transverse
 0.0065 cm/cm
@Thickness 3.20 mm
0.0065 in/in
@Thickness 0.126 in
Transverse
Linear Mold Shrinkage, Flow 0.0025 cm/cm0.0025 in/inParallel; Annealed; ISO 294-4
 0.0020 cm/cm
@Thickness 2.00 mm
0.0020 in/in
@Thickness 0.0787 in
Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0105 cm/cm0.0105 in/inNormal; Annealed; ISO 294-4
 0.0075 cm/cm
@Thickness 2.00 mm
0.0075 in/in
@Thickness 0.0787 in
Normal; ISO 294-4
Melt Index of Compound 6.0 g/10 min
@Load 2.16 kg,
Temperature 280 °C
6.0 g/10 min
@Load 4.76 lb,
Temperature 536 °F
cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 9595ASTM D785
 102102ISO 2039/2
Hardness, Rockwell R 120120ASTM D785
 122122ISO 2039/2
Tensile Strength at Break 170 MPa
@Temperature 23.0 °C
24700 psi
@Temperature 73.4 °F
ISO 527
Tensile Strength  55.2 MPa
@Temperature 150 °C
8010 psi
@Temperature 302 °F
ASTM D638
 86.5 MPa
@Temperature 90.0 °C
12500 psi
@Temperature 194 °F
ASTM D638
 172 MPa
@Temperature 23.0 °C
24900 psi
@Temperature 73.4 °F
ASTM D638
 210 MPa
@Temperature -40.0 °C
30500 psi
@Temperature -40.0 °F
ASTM D638
Tensile Stress  22.4 MPa
@Strain 0.470 %,
Temperature 150 °C
3250 psi
@Strain 0.470 %,
Temperature 302 °F
ISO 527
 27.22 MPa
@Strain 0.430 %,
Temperature 120 °C
3948 psi
@Strain 0.430 %,
Temperature 248 °F
ISO 527
 27.5 MPa
@Strain 0.160 %,
Temperature 0.000 °C
3990 psi
@Strain 0.160 %,
Temperature 32.0 °F
ISO 527
 28.39 MPa
@Strain 0.350 %,
Temperature 90.0 °C
4118 psi
@Strain 0.350 %,
Temperature 194 °F
ISO 527
 29.0 MPa
@Strain 0.140 %,
Temperature -40.0 °C
4210 psi
@Strain 0.140 %,
Temperature -40.0 °F
ISO 527
 30.0 MPa
@Strain 0.210 %,
Temperature 40.0 °C
4350 psi
@Strain 0.210 %,
Temperature 104 °F
ISO 527
 31.0 MPa
@Strain 0.180 %,
Temperature 23.0 °C
4500 psi
@Strain 0.180 %,
Temperature 73.4 °F
ISO 527
 34.9 MPa
@Strain 0.940 %,
Temperature 150 °C
5060 psi
@Strain 0.940 %,
Temperature 302 °F
ISO 527
 35.57 MPa
@Strain 0.310 %,
Temperature 60.0 °C
5159 psi
@Strain 0.310 %,
Temperature 140 °F
ISO 527
 41.5 MPa
@Strain 1.41 %,
Temperature 150 °C
6020 psi
@Strain 1.41 %,
Temperature 302 °F
ISO 527
 41.8 MPa
@Strain 0.830 %,
Temperature 120 °C
6060 psi
@Strain 0.830 %,
Temperature 248 °F
ISO 527
 45.7 MPa
@Strain 1.87 %,
Temperature 150 °C
6630 psi
@Strain 1.87 %,
Temperature 302 °F
ISO 527
 47.19 MPa
@Strain 0.690 %,
Temperature 90.0 °C
6844 psi
@Strain 0.690 %,
Temperature 194 °F
ISO 527
 49.1 MPa
@Strain 2.34 %,
Temperature 150 °C
7120 psi
@Strain 2.34 %,
Temperature 302 °F
ISO 527
 50.35 MPa
@Strain 0.370 %,
Temperature 40.0 °C
7303 psi
@Strain 0.370 %,
Temperature 104 °F
ISO 527
 50.8 MPa
@Strain 1.23 %,
Temperature 120 °C
7370 psi
@Strain 1.23 %,
Temperature 248 °F
ISO 527
 51.7 MPa
@Strain 2.81 %,
Temperature 150 °C
7500 psi
@Strain 2.81 %,
Temperature 302 °F
ISO 527
 52.4 MPa
@Strain 0.320 %,
Temperature 0.000 °C
7600 psi
@Strain 0.320 %,
Temperature 32.0 °F
ISO 527
 53.8 MPa
@Strain 3.28 %,
Temperature 150 °C
7800 psi
@Strain 3.28 %,
Temperature 302 °F
ISO 527
 53.9 MPa
@Strain 0.280 %,
Temperature -40.0 °C
7820 psi
@Strain 0.280 %,
Temperature -40.0 °F
ISO 527
 55.0 MPa
@Strain 0.520 %,
Temperature 60.0 °C
7980 psi
@Strain 0.520 %,
Temperature 140 °F
ISO 527
 55.6 MPa
@Strain 3.75 %,
Temperature 150 °C
8060 psi
@Strain 3.75 %,
Temperature 302 °F
ISO 527
 56.4 MPa
@Strain 0.350 %,
Temperature 23.0 °C
8180 psi
@Strain 0.350 %,
Temperature 73.4 °F
ISO 527
 56.85 MPa
@Strain 1.63 %,
Temperature 120 °C
8245 psi
@Strain 1.63 %,
Temperature 248 °F
ISO 527
 57.1 MPa
@Strain 4.21 %,
Temperature 150 °C
8280 psi
@Strain 4.21 %,
Temperature 302 °F
ISO 527
 58.5 MPa
@Strain 4.69 %,
Temperature 150 °C
8480 psi
@Strain 4.69 %,
Temperature 302 °F
ISO 527
 59.61 MPa
@Strain 1.03 %,
Temperature 90.0 °C
8646 psi
@Strain 1.03 %,
Temperature 194 °F
ISO 527
 61.26 MPa
@Strain 2.04 %,
Temperature 120 °C
8885 psi
@Strain 2.04 %,
Temperature 248 °F
ISO 527
 64.62 MPa
@Strain 2.44 %,
Temperature 120 °C
9372 psi
@Strain 2.44 %,
Temperature 248 °F
ISO 527
 67.28 MPa
@Strain 2.84 %,
Temperature 120 °C
9758 psi
@Strain 2.84 %,
Temperature 248 °F
ISO 527
 68.2 MPa
@Strain 1.37 %,
Temperature 90.0 °C
9890 psi
@Strain 1.37 %,
Temperature 194 °F
ISO 527
 69.36 MPa
@Strain 3.24 %,
Temperature 120 °C
10060 psi
@Strain 3.24 %,
Temperature 248 °F
ISO 527
 71.09 MPa
@Strain 3.65 %,
Temperature 120 °C
10310 psi
@Strain 3.65 %,
Temperature 248 °F
ISO 527
 71.87 MPa
@Strain 0.730 %,
Temperature 60.0 °C
10420 psi
@Strain 0.730 %,
Temperature 140 °F
ISO 527
 72.35 MPa
@Strain 4.05 %,
Temperature 120 °C
10490 psi
@Strain 4.05 %,
Temperature 248 °F
ISO 527
 72.8 MPa
@Strain 0.560 %,
Temperature 40.0 °C
10600 psi
@Strain 0.560 %,
Temperature 104 °F
ISO 527
 74.5 MPa
@Strain 0.480 %,
Temperature 23.0 °C
10800 psi
@Strain 0.480 %,
Temperature 73.4 °F
ISO 527
 74.52 MPa
@Strain 1.70 %,
Temperature 90.0 °C
10810 psi
@Strain 1.70 %,
Temperature 194 °F
ISO 527
 75.5 MPa
@Strain 0.420 %,
Temperature -40.0 °C
11000 psi
@Strain 0.420 %,
Temperature -40.0 °F
ISO 527
 75.9 MPa
@Strain 0.470 %,
Temperature 0.000 °C
11000 psi
@Strain 0.470 %,
Temperature 32.0 °F
ISO 527
 79.34 MPa
@Strain 2.04 %,
Temperature 90.0 °C
11510 psi
@Strain 2.04 %,
Temperature 194 °F
ISO 527
 83.14 MPa
@Strain 2.41 %,
Temperature 90.0 °C
12060 psi
@Strain 2.41 %,
Temperature 194 °F
ISO 527
 83.19 MPa
@Strain 0.940 %,
Temperature 60.0 °C
12070 psi
@Strain 0.940 %,
Temperature 140 °F
ISO 527
 85.76 MPa
@Strain 2.75 %,
Temperature 90.0 °C
12440 psi
@Strain 2.75 %,
Temperature 194 °F
ISO 527
 87.58 MPa
@Strain 3.09 %,
Temperature 90.0 °C
12700 psi
@Strain 3.09 %,
Temperature 194 °F
ISO 527
 88.92 MPa
@Strain 3.42 %,
Temperature 90.0 °C
12900 psi
@Strain 3.42 %,
Temperature 194 °F
ISO 527
 89.08 MPa
@Strain 0.730 %,
Temperature 40.0 °C
12920 psi
@Strain 0.730 %,
Temperature 104 °F
ISO 527
 92.13 MPa
@Strain 1.15 %,
Temperature 60.0 °C
13360 psi
@Strain 1.15 %,
Temperature 140 °F
ISO 527
 95.7 MPa
@Strain 0.560 %,
Temperature -40.0 °C
13900 psi
@Strain 0.560 %,
Temperature -40.0 °F
ISO 527
 97.24 MPa
@Strain 0.650 %,
Temperature 23.0 °C
14100 psi
@Strain 0.650 %,
Temperature 73.4 °F
ISO 527
 97.5 MPa
@Strain 0.630 %,
Temperature 0.000 °C
14100 psi
@Strain 0.630 %,
Temperature 32.0 °F
ISO 527
 105.4 MPa
@Strain 1.57 %,
Temperature 60.0 °C
15290 psi
@Strain 1.57 %,
Temperature 140 °F
ISO 527
 105.4 MPa
@Strain 0.920 %,
Temperature 40.0 °C
15290 psi
@Strain 0.920 %,
Temperature 104 °F
ISO 527
 110 MPa
@Strain 1.78 %,
Temperature 60.0 °C
16000 psi
@Strain 1.78 %,
Temperature 140 °F
ISO 527
 112.7 MPa
@Strain 1.99 %,
Temperature 60.0 °C
16350 psi
@Strain 1.99 %,
Temperature 140 °F
ISO 527
 114 MPa
@Strain 0.700 %,
Temperature -40.0 °C
16500 psi
@Strain 0.700 %,
Temperature -40.0 °F
ISO 527
 115.2 MPa
@Strain 2.20 %,
Temperature 60.0 °C
16710 psi
@Strain 2.20 %,
Temperature 140 °F
ISO 527
 115.41 MPa
@Strain 0.810 %,
Temperature 23.0 °C
16739 psi
@Strain 0.810 %,
Temperature 73.4 °F
ISO 527
 116.2 MPa
@Strain 1.08 %,
Temperature 40.0 °C
16850 psi
@Strain 1.08 %,
Temperature 104 °F
ISO 527
 116.5 MPa
@Strain 2.41 %,
Temperature 60.0 °C
16900 psi
@Strain 2.41 %,
Temperature 140 °F
ISO 527
 118 MPa
@Strain 0.790 %,
Temperature 0.000 °C
17100 psi
@Strain 0.790 %,
Temperature 32.0 °F
ISO 527
 127.1 MPa
@Strain 1.27 %,
Temperature 40.0 °C
18430 psi
@Strain 1.27 %,
Temperature 104 °F
ISO 527
 131.21 MPa
@Strain 0.980 %,
Temperature 23.0 °C
19030 psi
@Strain 0.980 %,
Temperature 73.4 °F
ISO 527
 132 MPa
@Strain 0.840 %,
Temperature -40.0 °C
19100 psi
@Strain 0.840 %,
Temperature -40.0 °F
ISO 527
 134.6 MPa
@Strain 1.47 %,
Temperature 40.0 °C
19520 psi
@Strain 1.47 %,
Temperature 104 °F
ISO 527
 135 MPa
@Strain 0.950 %,
Temperature 0.000 °C
19600 psi
@Strain 0.950 %,
Temperature 32.0 °F
ISO 527
 138.7 MPa
@Strain 1.63 %,
Temperature 40.0 °C
20120 psi
@Strain 1.63 %,
Temperature 104 °F
ISO 527
 142.1 MPa
@Strain 1.82 %,
Temperature 40.0 °C
20610 psi
@Strain 1.82 %,
Temperature 104 °F
ISO 527
 143.96 MPa
@Strain 1.15 %,
Temperature 23.0 °C
20880 psi
@Strain 1.15 %,
Temperature 73.4 °F
ISO 527
 150 MPa
@Strain 0.980 %,
Temperature -40.0 °C
21800 psi
@Strain 0.980 %,
Temperature -40.0 °F
ISO 527
 151 MPa
@Strain 1.11 %,
Temperature 0.000 °C
21900 psi
@Strain 1.11 %,
Temperature 32.0 °F
ISO 527
 153.65 MPa
@Strain 1.31 %,
Temperature 23.0 °C
22285 psi
@Strain 1.31 %,
Temperature 73.4 °F
ISO 527
 159.87 MPa
@Strain 1.44 %,
Temperature 23.0 °C
23187 psi
@Strain 1.44 %,
Temperature 73.4 °F
ISO 527
 166 MPa
@Strain 1.27 %,
Temperature 0.000 °C
24100 psi
@Strain 1.27 %,
Temperature 32.0 °F
ISO 527
 166.62 MPa
@Strain 1.61 %,
Temperature 23.0 °C
24166 psi
@Strain 1.61 %,
Temperature 73.4 °F
ISO 527
 167 MPa
@Strain 1.12 %,
Temperature -40.0 °C
24200 psi
@Strain 1.12 %,
Temperature -40.0 °F
ISO 527
 178 MPa
@Strain 1.45 %,
Temperature 0.000 °C
25800 psi
@Strain 1.45 %,
Temperature 32.0 °F
ISO 527
 184 MPa
@Strain 1.26 %,
Temperature -40.0 °C
26700 psi
@Strain 1.26 %,
Temperature -40.0 °F
ISO 527
 188 MPa
@Strain 1.58 %,
Temperature 0.000 °C
27300 psi
@Strain 1.58 %,
Temperature 32.0 °F
ISO 527
 200 MPa
@Strain 1.41 %,
Temperature -40.0 °C
29000 psi
@Strain 1.41 %,
Temperature -40.0 °F
ISO 527
Elongation at Break  1.7 %
@Temperature -40.0 °C
1.7 %
@Temperature -40.0 °F
ASTM D638
 1.8 %
@Temperature 23.0 °C
1.8 %
@Temperature 73.4 °F
ASTM D638
 1.8 %
@Temperature 23.0 °C
1.8 %
@Temperature 73.4 °F
ISO 527
 4.3 %
@Temperature 90.0 °C
4.3 %
@Temperature 194 °F
ASTM D638
 5.5 %
@Temperature 150 °C
5.5 %
@Temperature 302 °F
ASTM D638
Tensile Modulus  5.05 GPa
@Temperature 150 °C
732 ksi
@Temperature 302 °F
ASTM D638
 8.21 GPa
@Temperature 90.0 °C
1190 ksi
@Temperature 194 °F
ASTM D638
 16.5 GPa
@Temperature 23.0 °C
2390 ksi
@Temperature 73.4 °F
ASTM D638
 17.0 GPa
@Temperature 23.0 °C
2470 ksi
@Temperature 73.4 °F
ISO 527
 17.1 GPa
@Temperature -40.0 °C
2480 ksi
@Temperature -40.0 °F
ASTM D638
Flexural Strength  79.3 MPa
@Temperature 150 °C
11500 psi
@Temperature 302 °F
ASTM D790
 138 MPa
@Temperature 90.0 °C
20000 psi
@Temperature 194 °F
ASTM D790
 248 MPa
@Temperature 23.0 °C
36000 psi
@Temperature 73.4 °F
ASTM D790
 310 MPa
@Temperature -40.0 °C
45000 psi
@Temperature -40.0 °F
ASTM D790
Flexural Modulus  2.90 GPa
@Temperature 150 °C
421 ksi
@Temperature 302 °F
ASTM D790
 3.10 GPa
@Temperature 150 °C
450 ksi
@Temperature 302 °F
ISO 178
 6.89 GPa
@Temperature 90.0 °C
999 ksi
@Temperature 194 °F
ASTM D790
 6.90 GPa
@Temperature 93.0 °C
1000 ksi
@Temperature 199 °F
ISO 178
 14.5 GPa
@Temperature 23.0 °C
2100 ksi
@Temperature 73.4 °F
ASTM D790
 14.5 GPa
@Temperature 23.0 °C
2100 ksi
@Temperature 73.4 °F
ISO 178
 15.1 GPa
@Temperature -40.0 °C
2190 ksi
@Temperature -40.0 °F
ISO 178
 15.2 GPa
@Temperature -40.0 °C
2200 ksi
@Temperature -40.0 °F
ASTM D790
Compressive Strength 231 MPa
@Temperature 23.0 °C
33500 psi
@Temperature 73.4 °F
ASTM D695
Shear Strength 58.6 MPa
@Temperature 23.0 °C
8500 psi
@Temperature 73.4 °F
ASTM D732
Izod Impact, Notched  0.910 J/cm
@Temperature -40.0 °C
1.70 ft-lb/in
@Temperature -40.0 °F
ASTM D256
 0.960 J/cm
@Temperature 23.0 °C
1.80 ft-lb/in
@Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched  5.10 J/cm
@Temperature -40.0 °C
9.55 ft-lb/in
@Temperature -40.0 °F
ASTM D4812
 7.50 J/cm
@Temperature 23.0 °C
14.1 ft-lb/in
@Temperature 73.4 °F
ASTM D4812
Charpy Impact Unnotched  3.00 J/cm²
@Temperature -30.0 °C
14.3 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
 4.30 J/cm²
@Temperature 23.0 °C
20.5 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm²
@Temperature -30.0 °C
4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 1.00 J/cm²
@Temperature 23.0 °C
4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 15000 MPa
@Temperature 23.0 °C
2.18e+6 psi
@Temperature 73.4 °F
ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C
1.00e+15 ohm-cm
@Temperature 73.4 °F
ASTM D257
 >= 1.00e+15 ohm-cm
@Temperature 23.0 °C
>= 1.00e+15 ohm-cm
@Temperature 73.4 °F
IEC 60093
Surface Resistance  1.00e+13 ohm
@Temperature 23.0 °C
1.00e+13 ohm
@Temperature 73.4 °F
ASTM D257
 1.00e+15 ohm
@Temperature 23.0 °C
1.00e+15 ohm
@Temperature 73.4 °F
IEC 60093
Dielectric Constant  4.1
@Frequency 1000 Hz,
Temperature 23.0 °C
4.1
@Frequency 1000 Hz,
Temperature 73.4 °F
ASTM D150
 4.1
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
4.1
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
ASTM D150
 4.1
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
4.1
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength  12.0 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C
305 kV/in
@Thickness 0.126 in,
Temperature 302 °F
500 V/s, in oil; Short Time; ASTM D149
 13.5 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C
343 kV/in
@Thickness 0.0630 in,
Temperature 302 °F
500 V/s, in oil; Short Time; ASTM D149
 16.0 kV/mm
@Thickness 3.20 mm,
Temperature 95.0 °C
406 kV/in
@Thickness 0.126 in,
Temperature 203 °F
500 V/s, in oil; Short Time; ASTM D149
 17.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C
432 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F
500 V/s, in oil; Short Time; ASTM D149
 21.5 kV/mm
@Thickness 1.60 mm,
Temperature 95.0 °C
546 kV/in
@Thickness 0.0630 in,
Temperature 203 °F
500 V/s, in oil; Short Time; ASTM D149
 23.5 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C
597 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F
500 V/s, in oil; Short Time; ASTM D149
Dissipation Factor  0.0090
@Frequency 1000 Hz,
Temperature 23.0 °C
0.0090
@Frequency 1000 Hz,
Temperature 73.4 °F
ASTM D150
 0.017
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.017
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
ASTM D150
 0.017
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.017
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C
250 V
@Temperature 73.4 °F
IEC 60112
 250 - 400 V
@Temperature 23.0 °C
250 - 400 V
@Temperature 73.4 °F
UL 746A
 275 V
@Thickness 3.00 mm,
Temperature 23.0 °C
275 V
@Thickness 0.118 in,
Temperature 73.4 °F
UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C
278 µin/in-°F
@Temperature -40.0 - 73.4 °F
ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Temperature 73.4 - 131 °F
ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C
278 µin/in-°F
@Temperature 131 - 320 °F
ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C
278 µin/in-°F
@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C
278 µin/in-°F
@Temperature 131 - 320 °F
ISO 11359-1/-2
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ASTM E 831
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow  55.0 µm/m-°C
@Temperature -40.0 - 23.0 °C
30.6 µin/in-°F
@Temperature -40.0 - 73.4 °F
ASTM E 831
 55.0 µm/m-°C
@Temperature -40.0 - 23.0 °C
30.6 µin/in-°F
@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
 79.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
43.9 µin/in-°F
@Temperature 73.4 - 131 °F
ASTM E 831
 79.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
43.9 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1/-2
 96.0 µm/m-°C
@Temperature 55.0 - 160 °C
53.3 µin/in-°F
@Temperature 131 - 320 °F
ASTM E 831
 96.0 µm/m-°C
@Temperature 55.0 - 160 °C
53.3 µin/in-°F
@Temperature 131 - 320 °F
ISO 11359-1/-2
 85.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
47.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ASTM E 831
 85.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
47.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-1/-2
Melting Point 254 °C489 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 240 °C464 °FISO 75-1/-2
 247 °C477 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 224 °C435 °FASTM D648
 225 °C437 °FISO 75-1/-2
UL RTI, Electrical  150 °C
@Thickness 0.750 mm
302 °F
@Thickness 0.0295 in
UL 746B
 155 °C
@Thickness 1.50 mm
311 °F
@Thickness 0.0591 in
UL 746B
 155 °C
@Thickness 3.00 mm
311 °F
@Thickness 0.118 in
UL 746B
 155 °C
@Thickness 0.810 mm
311 °F
@Thickness 0.0319 in
UL 746B
UL RTI, Mechanical with Impact  155 °C
@Thickness 0.750 mm
311 °F
@Thickness 0.0295 in
UL 746B
 155 °C
@Thickness 0.810 mm
311 °F
@Thickness 0.0319 in
UL 746B
 155 °C
@Thickness 1.50 mm
311 °F
@Thickness 0.0591 in
UL 746B
 155 °C
@Thickness 3.00 mm
311 °F
@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact  155 °C
@Thickness 0.750 mm
311 °F
@Thickness 0.0295 in
UL 746B
 155 °C
@Thickness 1.50 mm
311 °F
@Thickness 0.0591 in
UL 746B
 155 °C
@Thickness 0.810 mm
311 °F
@Thickness 0.0319 in
UL 746B
 155 °C
@Thickness 3.00 mm
311 °F
@Thickness 0.118 in
UL 746B
Flammability, UL94  V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
IEC 60695-11-10
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
IEC 60695-11-10
 V-0
@Thickness 0.810 mm
V-0
@Thickness 0.0319 in
IEC 60695-11-10
 V-0
@Thickness 0.810 mm
V-0
@Thickness 0.0319 in
UL94
 V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
UL94
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
UL94
 5VA
@Thickness 1.50 mm
5VA
@Thickness 0.0591 in
IEC 60695-11-20
 5VA
@Thickness 3.00 mm
5VA
@Thickness 0.118 in
IEC 60695-11-10
 5VA
@Thickness 1.50 mm
5VA
@Thickness 0.0591 in
IEC 60695-11-10
 5VA
@Thickness 1.50 mm
5VA
@Thickness 0.0591 in
UL94
 5VA
@Thickness 3.00 mm
5VA
@Thickness 0.118 in
UL94
Oxygen Index 35 %35 %ASTM D2863
 35 %35 %ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 254 °C489 °F10°C/min; ISO 11357-1/-3
 280 °C536 °FOptimum
 270 - 290 °C518 - 554 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AdditiveFlame Retardant
AppearanceNatural Color
Contains Flame RetardantYes
Drying RecommendedYes
FeaturesDimensional Stability, Good
 Electrical Properties, Good
 Flame Retardant
 Stiffness, Good
 Strength, Good
 Thermal Aging Resistance, Good
FillerGlass fiber reinforcement
GenericPET
Heat StabilizedYes
Material StatusPreliminary Data
Part Marking Code>PET-GF43FR(17)<ISO 11469
Polymer FamilyPolyester
Polymer TypePET
Processing MethodInjection Molding
Product CategoryFlame Retardant Resins
 Glass Reinforced Resins
Resin IdentificationPET-GF43FR(17)ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAppliances
 Electrical Parts
 Electrical/Electronic Applications
 Phenolic Replacement
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38924.html

免责声明: 本文 DuPont Performance Polymers Rynite® FR543 NC010 PET 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4