- 密度 [g/cm3]: 1.61
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | ||
| Filler Content | 20 % | 20 % | |||
| Melt Index of Compound | 17 g/10 min @Load 2.16 kg, Temperature 280 °C | 17 g/10 min @Load 4.76 lb, Temperature 536 °F | cm3/10 min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 145 MPa @Temperature 23.0 °C | 21000 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | ISO 527 | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 200 V @Temperature 23.0 °C | 200 V @Temperature 73.4 °F | IEC 60112 | ||
| 250 V @Temperature 23.0 °C | 250 V @Temperature 73.4 °F | UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | ||
| 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | UL94 | |||
| V-2 @Thickness 0.750 mm | V-2 @Thickness 0.0295 in | UL94 | |||
| Glow Wire Test | 900 °C @Thickness 0.750 mm | 1650 °F @Thickness 0.0295 in | Ignition; IEC 60695-2-13 | ||
| 925 °C @Thickness 1.50 mm | 1700 °F @Thickness 0.0591 in | Ignition; IEC 60695-2-13 | |||
| 925 °C @Thickness 3.00 mm | 1700 °F @Thickness 0.118 in | Ignition; IEC 60695-2-13 | |||
| 950 °C @Thickness 0.750 mm | 1740 °F @Thickness 0.0295 in | IEC 60695-2-12 | |||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | IEC 60695-2-12 | |||
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 251 °C | 484 °F | 10°C/min; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | Optimum | |||
| 270 - 300 °C | 518 - 572 °F | ||||
| Mold Temperature | 130 - 140 °C | 266 - 284 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass fiber | ||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-GF20FR< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Color Stable Resins | ||||
| Flame Retardant Resins | |||||
| Glass Reinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-GF20FR | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||