- 密度 [g/cm3]: 1.73
- 弯曲模量 [MPa]: 9.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Melt Index of Compound | 70 g/10 min @Load 5.00 kg, Temperature 280 °C | 70 g/10 min @Load 11.0 lb, Temperature 536 °F | cm3/10 min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 9.70 GPa @Temperature 23.0 °C | 1410 ksi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5.00e+14 ohm-cm @Temperature 23.0 °C | 5.00e+14 ohm-cm @Temperature 73.4 °F | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm @Temperature 23.0 °C | >= 1.00e+15 ohm @Temperature 73.4 °F | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm @Temperature 23.0 °C | 813 kV/in @Temperature 73.4 °F | IEC 60243-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 33.9 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 78.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 43.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 110 µm/m-°C @Temperature 55.0 - 160 °C | 61.1 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 100 °C | 212 °F | 10°C/min; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 155 °C @Thickness 0.810 mm | 311 °F @Thickness 0.0319 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 155 °C @Thickness 0.810 mm | 311 °F @Thickness 0.0319 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 155 °C @Thickness 0.810 mm | 311 °F @Thickness 0.0319 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.810 mm | V-0 @Thickness 0.0319 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 247 °C | 477 °F | 10°C/min; ISO 11357-1/-3 | ||
| 270 - 290 °C | 518 - 554 °F | ||||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Drying Recommended | Yes | ||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PET-(MD+GF)40FR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Flame Retardant Resins | ||||
| Glass Reinforced Resins | |||||
| Resin Identification | PET-(MD+GF)40FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||