- 密度 [g/cm3]: 1.34
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 58.0
- 断裂伸长率 [%]: 80.0
- 弯曲模量 [MPa]: 2.40
- 硬度: 112.0
- 热变形温度 [℃]: 69.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D1505 | ||
| Bulk Density | 0.817 g/cc | 0.0295 lb/in³ | Poured; ASTM D1895 | ||
| 0.881 g/cc | 0.0318 lb/in³ | Vibrated; ASTM D1895 | |||
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| 1.40 g/cc | 0.0506 lb/in³ | Crystalline Density; ASTM D1505 | |||
| Melt Density | 1.20 g/cc @Temperature 285 °C | 0.0434 lb/in³ @Temperature 545 °F | ASTM D1238 | ||
| Particle Size | 2500 µm | 2500 µm | Pellet Size | ||
| Viscosity Measurement | 0.78 - 0.82 | 0.78 - 0.82 | Pellet, Intrinsic; VGAS-A-AN-G-V-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 112 | 112 | ASTM D785 | ||
| 114 | 114 | ISO 2039-2 | |||
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO 527 | ||
| 25.0 MPa | 3630 psi | ASTM D638 | |||
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | ISO 527 | ||
| 60.0 MPa | 8700 psi | ASTM D638 | |||
| Elongation at Break | 110 % | 110 % | ISO 527 | ||
| 110 % | 110 % | ASTM D638 | |||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 | ||
| 2.50 GPa | 363 ksi | ASTM D638 | |||
| Flexural Yield Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| 85.0 MPa | 12300 psi | ASTM D790 | |||
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 | ||
| 2.60 GPa | 377 ksi | ASTM D790 | |||
| Izod Impact, Notched | 0.270 J/cm @Temperature -40.0 °C | 0.506 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.360 J/cm @Temperature 23.0 °C | 0.674 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Izod Impact, Unnotched | NB | NB | ASTM D4812 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 3.10 kJ/m² @Temperature -40.0 °C | 1.48 ft-lb/in² @Temperature -40.0 °F | ISO 180 | ||
| 4.50 kJ/m² @Temperature 23.0 °C | 2.14 ft-lb/in² @Temperature 73.4 °F | ISO 180 | |||
| Puncture Energy | 0.800 J @Thickness 2.50 mm, Temperature -40.0 °C | 0.590 ft-lb @Thickness 0.0984 in, Temperature -40.0 °F | max load; ISO 6603-2 | ||
| 1.00 J @Thickness 3.20 mm, Temperature -40.0 °C | 0.738 ft-lb @Thickness 0.126 in, Temperature -40.0 °F | max load; ISO 6603-2 | |||
| 1.60 J @Thickness 2.50 mm, Temperature -40.0 °C | 1.18 ft-lb @Thickness 0.0984 in, Temperature -40.0 °F | max load; ASTM D3763 | |||
| 2.10 J @Thickness 3.20 mm, Temperature -40.0 °C | 1.55 ft-lb @Thickness 0.126 in, Temperature -40.0 °F | max load; ASTM D3763 | |||
| 15.0 J @Thickness 2.50 mm, Temperature 23.0 °C | 11.1 ft-lb @Thickness 0.0984 in, Temperature 73.4 °F | max load; ISO 6603-2 | |||
| 18.0 J @Thickness 3.20 mm, Temperature 23.0 °C | 13.3 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | max load; ISO 6603-2 | |||
| 26.0 J @Thickness 2.50 mm, Temperature 23.0 °C | 19.2 ft-lb @Thickness 0.0984 in, Temperature 73.4 °F | max load; ASTM D3763 | |||
| 31.0 J @Thickness 3.20 mm, Temperature 23.0 °C | 22.9 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | max load; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 56.0 J/g | 24.1 BTU/lb | ASTM E793 | ||
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | ASTM E1269 | ||
| 1.30 J/g-°C @Temperature 80.0 °C | 0.311 BTU/lb-°F @Temperature 176 °F | ASTM E1269 | |||
| 1.40 J/g-°C @Temperature 100 °C | 0.335 BTU/lb-°F @Temperature 212 °F | ASTM E1269 | |||
| 1.90 J/g-°C @Temperature 200 °C | 0.454 BTU/lb-°F @Temperature 392 °F | ASTM E1269 | |||
| 2.10 J/g-°C @Temperature 280 °C | 0.502 BTU/lb-°F @Temperature 536 °F | ASTM E1269 | |||
| Melting Point | 245 °C | 473 °F | Crystalline Peak Melting Point; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 | ||
| 69.0 °C | 156 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 | ||
| 67.0 °C | 153 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Acetaldehyde | <1ppm | VKCA-A-AS-G-GC-0001 | |||
| Color, CIE a* | -3.8 to -0.8 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE b* | -2.3 to 1.7 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE L* | 78 min | VGAS-A-AN-G-RS-001 | |||
| Fines, wt%, max | 0.05 | VGAS-A-AN-G-GA-1 | |||
| Pellet Shape | Cubical | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.