- 密度 [g/cm3]: 1.27
- 吸水率 [%]: 0.13
- 缺口冲击强度: 1.01
- 拉伸强度 [MPa]: 50.0
- 断裂伸长率 [%]: 68.0
- 弯曲强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 2.00
- 硬度: 109.0
- 热变形温度 [℃]: 70.0
- 透光率 [%]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 and ISO 1183D |
| Water Absorption | 0.13 % | 0.13 % | 24 hour immersion; ISO 62 |
| Moisture Vapor Transmission | 6.00 cc-mm/m²-24hr-atm | 15.2 cc-mil/100 in²-24hr-atm | F 372 Test conducted at 38°C (100°F) and 100% relative humidity. |
| Oxygen Transmission | 10.0 cc-mm/m²-24hr-atm | 25.4 cc-mil/100 in²-24hr-atm | ASTM D3985 |
| Viscosity Measurement | 0.70 | 0.70 | 0.7 for films per EMN-A-AC-G-V-1 |
| 0.70 | 0.70 | inherent viscosity of pellets | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 | 109 | ISO 2039-2 |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ISO 527 |
| Film Tensile Strength at Yield, MD | 52.0 MPa | 7540 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 52.0 MPa | 7540 psi | ASTM D882 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Yield, MD | 4.0 % | 4.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 4.0 % | 4.0 % | ASTM D882 |
| Elongation at Break | 100 % | 100 % | ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Secant Modulus, MD | 1.90 GPa | 276 ksi | ASTM D882 |
| Secant Modulus, TD | 1.90 GPa | 276 ksi | ASTM D882 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| 0.370 J/cm @Temperature -40.0 °C | 0.693 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Elmendorf Tear Strength, MD | 13.7 g/micron | 348 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 16.7 g/micron | 424 g/mil | ASTM D1922 |
| Dart drop Test | 400 g | 0.882 lb | Modified 12.7 mm (0.5 in.) dia. head, 127 mm (5 in.) dia. clamp, 660 mm (26 in.) drop. Value at -18°C (0°F) is 500 g.; ASTM D1709A |
| Film Tensile Strength at Break, MD | 59.0 MPa | 8560 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 55.0 MPa | 7980 psi | ASTM D882 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.4 @Frequency 1e+6 Hz | 2.4 @Frequency 1e+6 Hz | ASTM D 150 |
| 2.6 @Frequency 1000 Hz | 2.6 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | Short Time, 500 V/sec rate-of-rise; ASTM D 149 |
| Dissipation Factor | 0.0050 @Frequency 1000 Hz | 0.0050 @Frequency 1000 Hz | ASTM D150 |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 | |
| Arc Resistance | 143 sec | 143 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 51.0 µm/m-°C @Temperature -30.0 - 40.0 °C | 28.3 µin/in-°F @Temperature -22.0 - 104 °F | ASTM D696 |
| Specific Heat Capacity | 1.30 J/g-°C @Temperature 60.0 °C | 0.311 BTU/lb-°F @Temperature 140 °F | |
| 1.76 J/g-°C @Temperature 100 °C | 0.421 BTU/lb-°F @Temperature 212 °F | ||
| 1.88 J/g-°C @Temperature 150 °C | 0.449 BTU/lb-°F @Temperature 302 °F | ||
| 1.97 J/g-°C @Temperature 200 °C | 0.471 BTU/lb-°F @Temperature 392 °F | ||
| 2.05 J/g-°C @Temperature 250 °C | 0.490 BTU/lb-°F @Temperature 482 °F | ||
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | DSC |
| Optical Properties | Metric | English | Comments |
| Haze | 0.80 % | 0.80 % | ASTM D1003 |
| Gloss | 108 % | 108 % | at 45°; ASTM D 2457 |
| Transmission, Visible | 85 % | 85 % | per ASTM D1746 |
| 89 % | 89 % | Regular transmittance per ASTM D 1003 Modified. | |
| 91 % | 91 % | Total Transmittance; ASTM D 1003 | |