- 拉伸强度 [MPa]: 52.0
- 断裂伸长率 [%]: 74.0
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 1.90
- 硬度: 114.0
- 热变形温度 [℃]: 96.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO 527 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527 |
| Elongation at Break | 120 % | 120 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | ISO 178 |
| 79.0 MPa | 11500 psi | ASTM D790 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| 1.39 J/cm @Temperature -40.0 °C | 2.60 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.4 @Frequency 1e+6 Hz | 2.4 @Frequency 1e+6 Hz | ASTM D 150 |
| 2.6 @Frequency 1000 Hz | 2.6 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 17.3 kV/mm | 439 kV/in | Short Time, 500 V/sec rate-of-rise; ASTM D 149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | ASTM D150 |
| 0.0080 @Frequency 1e+6 Hz | 0.0080 @Frequency 1e+6 Hz | ASTM D150 | |
| Arc Resistance | 142 sec | 142 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D3638 |
| High Voltage Arc-Tracking Rate, HVTR | 17.7 mm/min | 0.697 in/min | UL 746A |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.34 J/g-°C @Temperature 60.0 °C | 0.320 BTU/lb-°F @Temperature 140 °F | |
| 2.60 J/g-°C @Temperature 240 °C | 0.621 BTU/lb-°F @Temperature 464 °F | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ASTM D648 and ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 and ISO 75 |
| Vicat Softening Point | 108 °C | 226 °F | 5 kg load; ISO 306 |
| 119 °C | 246 °F | 1 kg load; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 292.5 °C | 558.5 °F | |
| Mold Temperature | 37.5 °C | 99.5 °F | |
| Drying Temperature | 95.0 °C | 203 °F | |
| Dry Time | 5 hour | 5 hour | |