- 密度 [g/cm3]: 1.18
- 拉伸强度 [MPa]: 50.0
- 热变形温度 [℃]: 104.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 5.3 % | 5.3 % | |
| Tensile Modulus | 1.82 GPa | 264 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 6.30 J/cm² | 30.0 ft-lb/in² | Partial Break |
| 2.08 J/cm² @Temperature -30.0 °C | 9.90 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 74.0 µm/m-°C @Temperature 20.0 °C | 41.1 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature 20.0 °C | 28.3 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.51 J/g-°C | 0.361 BTU/lb-°F | |
| Melting Point | 280 °C | 536 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | |
| Vicat Softening Point | 108 °C | 226 °F | |
| Glass Transition Temp, Tg | 112 °C | 234 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 295 - 330 °C | 563 - 626 °F | |