- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.55
- 弯曲强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 5.20
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Water Absorption | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 84 | 84 | ISO 2039 |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.1 @Frequency 100000 Hz | 3.1 @Frequency 100000 Hz | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.17 mm | 533 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 100000 Hz | 0.010 @Frequency 100000 Hz | ASTM D150 |
| Arc Resistance | 119 sec | 119 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.12 µm/m-°C @Temperature 100 °C | 8.400 µin/in-°F @Temperature 212 °F | Flow Direction; ASTM E831 |
| 34.2 µm/m-°C @Temperature 20.0 °C | 19.0 µin/in-°F @Temperature 68.0 °F | Flow Direction; ASTM E831 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature 100 °C | 26.0 µin/in-°F @Temperature 212 °F | ASTM E831 |
| 76.0 µm/m-°C @Temperature 20.0 °C | 42.2 µin/in-°F @Temperature 68.0 °F | ASTM E831 | |
| Melting Point | 248 °C | 478 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 280 °C | 518 - 536 °F | Injection; barrel center zone temperature |