- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.38
- 弯曲强度 [MPa]: 97.0
- 弯曲模量 [MPa]: 5.20
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.090 % | 0.090 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 81 | 81 | ISO 2039 |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ISO 527 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.2 @Frequency 100000 Hz | 3.2 @Frequency 100000 Hz | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.17 mm | 533 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 100000 Hz | 0.010 @Frequency 100000 Hz | ASTM D150 |
| Arc Resistance | 101 sec | 101 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 23.4 µm/m-°C @Temperature 100 °C | 13.0 µin/in-°F @Temperature 212 °F | Flow Direction; ASTM E831 |
| 37.8 µm/m-°C @Temperature 20.0 °C | 21.0 µin/in-°F @Temperature 68.0 °F | Flow Direction; ASTM E831 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature 20.0 °C | 32.8 µin/in-°F @Temperature 68.0 °F | ASTM E831 |
| 84.6 µm/m-°C @Temperature 100 °C | 47.0 µin/in-°F @Temperature 212 °F | ASTM E831 | |
| Melting Point | 249 °C | 480 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 280 °C | 518 - 536 °F | Injection; barrel center zone temperature |