- 密度 [g/cm3]: 1.79
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.58
- 断裂伸长率 [%]: 178.1
- 弯曲强度 [MPa]: 122.2
- 弯曲模量 [MPa]: 11.11
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 122.2 MPa | 17720 psi | ASTM D638 |
| Elongation at Break | 1.68 % | 1.68 % | ASTM D638 |
| Tensile Modulus | 12.53 GPa | 1817 ksi | ASTM D638 |
| Flexural Yield Strength | 178.1 MPa | 25830 psi | ASTM D790 |
| Flexural Modulus | 11.11 GPa | 1611 ksi | ASTM D790 |
| Compressive Yield Strength | 154.9 MPa | 22470 psi | ASTM D695 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.10e+16 ohm-cm | 1.10e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 15.5 kV/mm | 394 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1e+6 Hz | 0.013 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 40 sec | 40 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |