- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.66
- 断裂伸长率 [%]: 215.6
- 弯曲强度 [MPa]: 147.8
- 弯曲模量 [MPa]: 10.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0013 cm/cm | 0.0013 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 147.8 MPa | 21440 psi | ASTM D638 |
| Elongation at Break | 1.77 % | 1.77 % | ASTM D638 |
| Tensile Modulus | 10.56 GPa | 1532 ksi | ASTM D638 |
| Flexural Yield Strength | 215.6 MPa | 31270 psi | ASTM D790 |
| Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
| Compressive Yield Strength | 174.6 MPa | 25320 psi | ASTM D695 |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 9.23e+17 ohm-cm | 9.23e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.3 kV/mm | 414 kV/in | Short Time; ASTM D149 |
| 17.0 kV/mm | 432 kV/in | Step by Step; ASTM D149 | |
| Dissipation Factor | 0.012 @Frequency 1e+6 Hz | 0.012 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 60 sec | 60 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |