- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.72
- 断裂伸长率 [%]: 227
- 弯曲强度 [MPa]: 144.1
- 弯曲模量 [MPa]: 9.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 144.1 MPa | 20900 psi | ASTM D638 |
| Elongation at Break | 1.72 % | 1.72 % | ASTM D638 |
| Tensile Modulus | 10.14 GPa | 1471 ksi | ASTM D638 |
| Flexural Yield Strength | 227 MPa | 32900 psi | ASTM D790 |
| Flexural Modulus | 9.96 GPa | 1440 ksi | ASTM D790 |
| Compressive Yield Strength | 185.1 MPa | 26850 psi | ASTM D695 |
| Izod Impact, Notched | 0.720 J/cm | 1.35 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 18.2 kV/mm | 462 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 70 sec | 70 sec | ASTM D495 |
| Comparative Tracking Index | 225 V | 225 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |