- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.39
- 断裂伸长率 [%]: 127.4
- 弯曲强度 [MPa]: 96.3
- 弯曲模量 [MPa]: 6.43
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 96.3 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 1.61 % | 1.61 % | ASTM D638 |
| Tensile Modulus | 6.79 GPa | 985 ksi | ASTM D638 |
| Flexural Yield Strength | 127.4 MPa | 18480 psi | ASTM D790 |
| Flexural Modulus | 6.43 GPa | 933 ksi | ASTM D790 |
| Compressive Yield Strength | 154.5 MPa | 22410 psi | ASTM D695 |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.20e+16 ohm-cm | 2.20e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz | 2.9 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 15.8 kV/mm | 401 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |