- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.04
- 缺口冲击强度: 1.07
- 断裂伸长率 [%]: 234
- 弯曲强度 [MPa]: 151.9
- 弯曲模量 [MPa]: 14.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 151.9 MPa | 22030 psi | ASTM D638 |
| Elongation at Break | 1.19 % | 1.19 % | ASTM D638 |
| Tensile Modulus | 14.86 GPa | 2155 ksi | ASTM D638 |
| Flexural Yield Strength | 234 MPa | 33900 psi | ASTM D790 |
| Flexural Modulus | 14.21 GPa | 2061 ksi | ASTM D790 |
| Compressive Yield Strength | 171.4 MPa | 24860 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.92e+16 ohm-cm | 2.92e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.1 kV/mm | 409 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz | 0.010 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 60 sec | 60 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |