- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.05
- 缺口冲击强度: 1.08
- 断裂伸长率 [%]: 294
- 弯曲强度 [MPa]: 186.2
- 弯曲模量 [MPa]: 14.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 186.2 MPa | 27010 psi | ASTM D638 |
| Elongation at Break | 1.74 % | 1.74 % | ASTM D638 |
| Flexural Yield Strength | 294 MPa | 42600 psi | ASTM D790 |
| Flexural Modulus | 14.07 GPa | 2041 ksi | ASTM D790 |
| Compressive Yield Strength | 179.2 MPa | 25990 psi | ASTM D695 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.70e+16 ohm-cm | 1.70e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz | 3.4 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 18.6 kV/mm | 472 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 100 sec | 100 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |