- 熔体流动速率 [g/10min]: 18.0
- 缺口冲击强度: 8.54
- 拉伸强度 [MPa]: 53.1
- 弯曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 3.80 kg, Temperature 260 °C | 18 g/10 min @Load 8.38 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 41.4 MPa | 6000 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 180 % | 180 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Temperature 22.8 °C | 16.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 |