- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.84
- 断裂伸长率 [%]: 248.8
- 弯曲强度 [MPa]: 164.7
- 弯曲模量 [MPa]: 10.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00070 cm/cm | 0.00070 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 164.7 MPa | 23890 psi | ASTM D638 |
| Elongation at Break | 2.17 % | 2.17 % | ASTM D638 |
| Tensile Modulus | 11.27 GPa | 1635 ksi | ASTM D638 |
| Flexural Yield Strength | 248.8 MPa | 36090 psi | ASTM D790 |
| Flexural Modulus | 10.13 GPa | 1469 ksi | ASTM D790 |
| Compressive Yield Strength | 182.7 MPa | 26500 psi | ASTM D695 |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.70e+17 ohm-cm | 1.70e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.1 @Frequency 1e+6 Hz | 2.1 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 19.5 kV/mm | 495 kV/in | Short Time; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | 225 V | 225 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |