- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.747
- 弯曲模量 [MPa]: 6.89
- 硬度: 118.0
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D 792 |
| Water Absorption | 0.0600 % | 0.0600 % | ASTM D 570 |
| Linear Mold Shrinkage | 0.00300 cm/cm | 0.00300 in/in | ASTM D 696 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D 785 |
| Tensile Strength | 117.2 MPa | 17000 psi | ASTM D 638 |
| Elongation at Break | 3.00 % | 3.00 % | ASTM D 638 |
| Flexural Strength | 182.8 MPa | 26510 psi | ASTM D 790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D 648 |