- 密度 [g/cm3]: 1.18
- 缺口冲击强度: 10.1
- 弯曲模量 [MPa]: 1.59
- 硬度: 119.0
- 热变形温度 [℃]: 98.9
- 透光率 [%]: 85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 34 | 34 | ASTM D785 | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength | 49.6 MPa | 7200 psi | ASTM D638 | ||
| Tensile Modulus | 1.59 GPa | 230 ksi | ASTM D638 | ||
| Flexural Strength | 65.5 MPa | 9500 psi | ASTM D790 | ||
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D790 | ||
| Compressive Strength | 98.6 MPa | 14300 psi | ASTM D695 | ||
| Izod Impact, Notched | 10.1 - 10.7 J/cm @Thickness <=3.00 mm | 19.0 - 20.0 ft-lb/in @Thickness <=0.118 in | ASTM D256A | ||
| Izod Impact Unnotched | NB @Thickness <=3.00 mm | NB @Thickness <=0.118 in | ASTM D256A | ||
| Impact Test | >= 22.6 J @Thickness 5.99 mm, Temperature 22.8 °C | >= 16.7 ft-lb @Thickness 0.236 in, Temperature 73.0 °F | drop Ball Impact Test, 1 inch dart | ||
| >= 22.6 J @Thickness 5.99 mm, Temperature -17.8 °C | >= 16.7 ft-lb @Thickness 0.236 in, Temperature 0.000 °F | drop Ball Impact Test, 1 inch dart | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.2 µm/m-°C @Temperature -34.4 - -1.11 °C | 39.0 µin/in-°F @Temperature -30.0 - 30.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 85 % | 85 % | ASTM D1003 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 154 - 182 °C | 310 - 360 °F | Forming Temp | ||
| Descriptive Properties | |||||
| Flammability | B2 | ||||