- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.67
- 缺口冲击强度: 8.5
- 拉伸强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 10.0
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 280 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 536 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 11.16 GPa | 1619 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | IEC 60250 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Glow Wire Test | 960 °C | 1760 °F | GWFI; IEC 60695 |