- 密度 [g/cm3]: 1.67
- 吸水率 [%]: 0.5
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 9.00
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | DIN 53479 |
| Water Absorption | 0.50 % | 0.50 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C | 1.87 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | VDE 0303/4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |