- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.42
- 缺口冲击强度: 0.82
- 拉伸强度 [MPa]: 55.0
- 断裂伸长率 [%]: 92.0
- 弯曲模量 [MPa]: 2.70
- 热变形温度 [℃]: 128.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D 792 | ||
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.42 % @Temperature 23.0 °C | 0.42 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0065 - 0.0075 cm/cm @Thickness 3.20 mm | 0.0065 - 0.0075 in/in @Thickness 0.126 in | SABIC Method | ||
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 250 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D 1238 | ||
| 17 g/10 min @Load 2.16 kg, Temperature 265 °C | 17 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |||
| 19 g/10 min @Load 2.16 kg, Temperature 265 °C | 19 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 | ||
| 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 | |||
| 45.0 MPa | 6530 psi | Type I, 10 mm/min; SABIC - Japan Method | |||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | ||
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D 638 | |||
| 56.0 MPa | 8120 psi | Type I, 10 mm/min; SABIC - Japan Method | |||
| Elongation at Break | 12.1 % | 12.1 % | 5 mm/min; ISO 527 | ||
| 38.7 % | 38.7 % | Type I, 5 mm/min; ASTM D 638 | |||
| 100 % | 100 % | Type I, 10 mm/min; SABIC - Japan Method | |||
| Elongation at Yield | 4.1 % | 4.1 % | 5 mm/min; ISO 527 | ||
| 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D 638 | |||
| 67 % | 67 % | Type I, 10 mm/min; SABIC - Japan Method | |||
| Tensile Modulus | 3.19 GPa | 463 ksi | 1 mm/min; ISO 527 | ||
| 3.23 GPa | 468 ksi | 5 mm/min; ASTM D 638 | |||
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | ||
| 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 | |||
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 | ||
| 2.99 GPa | 434 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |||
| Izod Impact, Notched | 0.820 J/cm @Temperature -30.0 °C | 1.54 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | ||
| 0.870 J/cm @Temperature 23.0 °C | 1.63 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | ||
| 7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| Impact Test | 54.0 J @Temperature 23.0 °C | 39.8 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 58.1 µm/m-°C @Temperature -30.0 - 80.0 °C | 32.3 µin/in-°F @Temperature -22.0 - 176 °F | ISO 11359-2 | ||
| 58.6 µm/m-°C @Temperature -40.0 - 60.0 °C | 32.6 µin/in-°F @Temperature -40.0 - 140 °F | ASTM E 831 | |||
| CTE, linear, Transverse to Flow | 70.1 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| 70.5 µm/m-°C @Temperature -40.0 - 60.0 °C | 39.2 µin/in-°F @Temperature -40.0 - 140 °F | ASTM E 831 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| 129 °C @Thickness 3.20 mm | 264 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |||
| 134 °C @Thickness 6.40 mm | 273 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 109 °C @Thickness 3.20 mm | 228 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |||
| 121 °C @Thickness 6.40 mm | 250 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |||
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ASTM D 1525 | ||
| 137 °C | 279 °F | Rate B/50; ISO 306 | |||
| 140 °C | 284 °F | Rate B/120; ISO 306 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 | |||