- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.26
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 5.00
- 硬度: 119.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.26 % @Temperature 23.0 °C | 0.26 % @Temperature 73.4 °F | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on tensile bar; SABIC Method | ||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on tensile bar; SABIC Method | ||
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 265 °C | 12 g/10 min @Load 2.65 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ISO 2039-2 | ||
| Hardness, H358/30 | 101 MPa | 14600 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 135 MPa | 19600 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | ||
| 25.0 kJ/m² @Temperature -30.0 °C | 11.9 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| 3.00 J/cm² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/2C | |||
| 0.600 J/cm² @Temperature -20.0 °C | 2.86 ft-lb/in² @Temperature -4.00 °F | ISO 179/2C | |||
| Taber Abrasion, mg/1000 Cycles | 17 @Load 1.00 kg | 17 @Load 2.20 lb | CS-17; SABIC Method | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.0 @Frequency 50.0 - 60.0 Hz | 3.0 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm | 406 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| 18.0 kV/mm @Thickness 1.00 mm | 457 kV/in @Thickness 0.0394 in | short time; IEC 60243-1 | |||
| 24.0 kV/mm @Thickness 1.60 mm | 610 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |||
| 30.0 kV/mm @Thickness 0.800 mm | 762 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz | 0.0010 @Frequency 50.0 - 60.0 Hz | IEC 60250 | ||
| 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | |||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | >= 175 V | >= 175 V | IEC 60112 | ||
| 325 V | 325 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 30.6 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 47.2 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 | ||
| 213 °C | 415 °F | Rate B/120; ISO 306 | |||
| 220 °C | 428 °F | Rate A/50; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL 94 by SABIC-IP | ||
| Glow Wire Test | 750 °C @Thickness 1.00 mm | 1380 °F @Thickness 0.0394 in | Glow Wire Flammability Index; IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||