SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific)物性表参数

熔体流动速率 [g/10min]: 12.0
密度 [g/cm3]: 1.18
缺口冲击强度: 9.0
拉伸强度 [MPa]: 55.0
断裂伸长率 [%]: 84.0
弯曲模量 [MPa]: 1.96
热变形温度 [℃]: 96.0
透光率 [%]: 88.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D 792
Density	1.18 g/cc	0.0426 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 265 °C	12 g/10 min @Load 4.76 lb, Temperature 509 °F	ASTM D 1238
	12 g/10 min @Load 2.16 kg, Temperature 265 °C	12 g/10 min @Load 4.76 lb, Temperature 509 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	75	75	10S reading; ASTM D 2240
Tensile Strength at Break	56.0 MPa	8120 psi	Type I, 50 mm/min; ASTM D 638
	56.0 MPa	8120 psi	50 mm/min; ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D 638
	55.0 MPa	7980 psi	50 mm/min; ISO 527
Elongation at Break	135 %	135 %	Type I, 50 mm/min; ASTM D 638
	>= 150 %	>= 150 %	50 mm/min; ISO 527
Elongation at Yield	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D 638
	5.0 %	5.0 %	5 mm/min; ISO 527
Tensile Modulus	1.88 GPa	273 ksi	50 mm/min; ASTM D 638
	2.00 GPa	290 ksi	1 mm/min; ISO 527
Flexural Strength	75.0 MPa	10900 psi	break, 2 mm/min; ISO 178
Flexural Yield Strength	84.0 MPa	12200 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	1.96 GPa	284 ksi	1.3 mm/min, 50 mm span; ASTM D 790
	2.00 GPa	290 ksi	2 mm/min; ISO 178
Izod Impact, Notched	9.00 J/cm @Temperature 23.0 °C	16.9 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature -10.0 °C	2.38 ft-lb/in² @Temperature 14.0 °F	80104; ISO 180/1A
	8.00 kJ/m² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Impact Test	95.0 J @Temperature 23.0 °C	70.1 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	ASTM D 257
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ASTM D 257
Comparative Tracking Index	>= 600 V	>= 600 V	PLC code 0; UL 746A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 23.0 - 60.0 °C	44.4 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
	105 µm/m-°C @Temperature -40.0 - 40.0 °C	58.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	80.0 µm/m-°C @Temperature 23.0 - 60.0 °C	44.4 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
	105 µm/m-°C @Temperature -40.0 - 40.0 °C	58.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
Thermal Conductivity	0.230 W/m-K	1.60 BTU-in/hr-ft²-°F	ISO 8302
Hot Ball Pressure Test	<= 105 °C	<= 221 °F	IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi)	96.0 °C @Thickness 3.20 mm	205 °F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	99.0 °C	210 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	90.0 °C @Thickness 3.20 mm	194 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	115 °C	239 °F	Rate B/50; ASTM D 1525
	115 °C	239 °F	Rate B/120; ISO 306
Flammability, UL94	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in	UL 94
Glow Wire Test	750 °C @Thickness 1.00 mm	1380 °F @Thickness 0.0394 in	Glow Wire Flammability Index; IEC 60695-2-12

Optical Properties	Metric	English	Comments
Refractive Index	1.557	1.557	ISO 489
Haze	1.1 % @Thickness 2.54 mm	1.1 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible	88 % @Thickness 2.54 mm	88 % @Thickness 0.100 in	ASTM D 1003