- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.25
- 拉伸强度 [MPa]: 150.0
- 断裂伸长率 [%]: 215
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % @Temperature 23.0 °C | 0.25 % @Temperature 73.4 °F | ISO 62 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U |
| 40.0 kJ/m² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 11.1 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 44.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ISO 306 |
| 240 °C | 464 °F | Rate B/120; ISO 306 | |